以锐钛矿型TiO2纳米粉体为载体,Na2SiO3为包覆剂,H2SO4为中和剂,采用溶胶-凝胶法制备了系列环境净化功能TiO2/SiO2复合纳米粉体.用XRD、XRF、TEM、BET比表面分析对其进行了表征,并以亚甲基蓝溶液的光催化降解率和COD去除率为指标评价了其光催化活性.结果表明,在TiO2纳米颗粒表面包覆一层多孔非晶态水合二氧化硅纳米膜,可以显著提高其水分散性,有效控制其光催化活性,进而提高了涂料的抗老化性和耐候性.中和时间对包硅效率影响较大,适当增加中和时间有利于提高包硅效率;包覆温度对包硅效率影响较小,升高温度使包硅效率略有降低.低温包覆,成膜相对疏松,改性粉体的光催化活性相对较高;高温包覆,成膜相对致密,改性粉体的光催化活性相对较低.
参考文献
| [1] | Hu Chun;Wang Yizhong;Tang Hongxiao .Preparation and characterization of surface bond-conjugated TiO_2/SiO_2 and photocatalysis for azo dyes[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2001(3/4):277-285. |
| [2] | Choi W;Ko J Y;Park H et al.[J].Applied Catalysis B:Environmental,2001,31:209-220. |
| [3] | Chao H E;Yun Y U;H U Xingfang et al.[J].Journal of the European Ceramic Society,2003,23:1457-1464. |
| [4] | Huang Zheng;Maness P C;Blake D M et al.[J].Journal of Photochemistry and Photobiology A:Chemistry,2000,130:163-170. |
| [5] | Fu Xianzhi;Clark L A;Yang Qing et al.[J].Environmental Science and Technology,1996,30:647-653. |
| [6] | Choi Wonyong;Ko Joung Yun;Park Hyunwoong et al.[J].Applied Catalysis B:Environmental,2001,31:209-220. |
| [7] | van Dyk AC.;Heyns AM. .Dispersion stability and photo-activity of rutile (TiO2) powders[J].Journal of Colloid and Interface Science,1998(2):381-391. |
| [8] | 姜洪泉;王鹏;钟敏.[J].高校化学工程学报,2004 |
| [9] | 程银兵,马建华,吴广明,沈军,王珏.热处理对溶胶-凝胶TiO2薄膜的晶相转变和性能影响[J].功能材料,2003(01):73-75. |
| [10] | 沈钟;王国庭.胶体与表面化学[M].北京:化学工业出版社,1997 |
| [11] | 许秋颖 .纳米TiO2环境功能涂料的制备与表征[D].哈尔滨:哈尔滨工业大学,2003. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%