考察了等离子喷涂Ｃｒ３Ｃ２－ＮｉＣｒ涂层及其表面化学镀Ｎｉ镀层通过不同配副组成摩擦副的摩擦学特性，并应用ＳＥＭ、ＸＲＤ和ＸＰＳ对磨痕进行了分析．结果发现：等离子喷涂Ｃｒ３Ｃ２－ＮｉＣｒ涂层及其表面化学镀Ｎｉ镀层自配副组成摩擦副，均表现出较大的摩擦系数和磨损系数；但是，Ｃｒ３Ｃ２－ＮｉＣｒ涂层表面化学镀Ｎｉ镀层与Ｃｒ３Ｃ２－ＮｉＣｒ涂层配副组成摩擦副，在于摩擦条件下，能达到０．１２的摩擦系数和接近１０－６ｍｍ3（Ｎｍ）－１的磨损系数．上述结果是由于Ｃｒ３Ｃ２－ＮｉＣｒ涂层的磨损机理从强烈的层状颗粒剥落转变为沿气孔和微裂纹等处的颗粒断裂．
Tribological properties of plasma-sprayed Cr3C2-NiCr coatings without or with electroless plated
Ni were investigated, and the worn surfaces were analyzed by employing SEM, XRD and XPS. It was found that both the self-mated rubbing pairs consisting
of the Cr3C2-NiCr coating and the Cr3C2-NiCr coating electroless plated with Ni displayed higher friction coefficient and wear coefficient.
However, The rubbing pair of the Cr3C2-NiCr coating electroless plated with Ni against the Cr3C2-NiCr coating had a friction
coefficient of 0.12 and a wear coefficient close to 10-6mm3(Nm)-1 even if under dry sliding. The improvement in tribological properties
could be attributed to that the wear mechanism of Cr3C2-NiCr coating transformed to particle fracturing along pores and microcracks from the
intensive spalling along splat interfaces.