为了优化TiAl合金的使用性能,本文研究了热等静压后的PM-TiAl基合金经过热处理后显微组织的变化情况及力学性能,发现其在热处理温度为1 355℃为全片层组织,在1 335℃为双态组织.全片层组织常温下的抗拉强度为446 MPa,随着温度的升高而增加；屈服强度为386 MPa,随着温度的升高而降低.
参考文献
| [1] | 张绪虎,郎泽保.TiAl金属间化合物粉末冶金制备技术研究[J].宇航材料工艺,2007(05):53-55,66. |
| [2] | 刘咏,黄伯云,周科朝,贺跃辉.热等静压对粉末冶金TiAl 合金显微组织和相成分的影响[J].粉末冶金技术,2001(03):165-169. |
| [3] | Chan K S;Kim Y W .Influence of microstructure on cracktip micromechanics and fracture behaviors of a two-phase TiAI alloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23A(06):1663-1677. |
| [4] | Campbell J P;Venkateswara K T;Rithchie R O .The effect of microstructure on fracture toughness and fatigue crack growth behavior in γ-titanium aluminide based intermetallics[J].Metall Materal Trans A,1993,30A(31):563-577. |
| [5] | Chan K S .Toughening mechanisms in titanium aluminides[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24A(03):569-583. |
| [6] | McCullough C;Valencia J J;Levi C G et al.Phase equilibria and solidification in Ti-Al alloys[J].Acta Metallurgica,1989,37(05):1321-1336. |
| [7] | Chen W R;Triantafillou J;Beddoes J.Effect of fully lamellar morphology on creep of a near γ-TiA1 intermetallic[J].Intermetallics,1999(07):171-178. |
| [8] | Chen W R;Triantafillou J;Beddoes J et al.Effect of fully lamellar morphology on creep of a near γ-TiA1 intermetallic[J].Intermetallics,1999,7(02):171-178. |
| [9] | Huang S C;HallE L .The effects of Cr additions to binary TiAl-base alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22A(09):2619-2627. |
| [10] | Yoshihara M;Miura K .Effects of Nb addition on oxidation behavior of TiA1[J].Intermetallics,1995,3(05):357-363. |
| [11] | 陈进;黄伯云;曲选辉 .热处理对TiAl基合金的组织结构和室温性能的影响[J].中南矿冶学院学报,1993,24(03):378-383. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%