采用阴极恒电压法在ITO导电玻璃上沉积了ZnS薄膜,并用X射线衍射仪(XRD)、原子力显微镜(AFM)以及紫外/可见/近红外光谱仪对薄膜的结构和性能进行了表征,研究了pH值对薄膜的相组成、显微形貌以及光学性质的影响.结果表明:在pH=4,沉积时间为20 min,沉积电压为2 V,加入柠檬酸钠作络合剂的情况下,得到沿(200)晶面生长的立方相ZnS薄膜,薄膜组成均匀而致密,随pH值增加,禁带宽度降低.
参考文献
| [1] | 憨勇;郑修麟;刘正堂 .ZnS的不同制备方法及性能的对比[J].材料导报,1995,9(04):35-38. |
| [2] | 王和明,蔡以超,杨曜源,东燕萍,王永杰,闫泽武.CVD方法生长平面和曲面块状多晶硫化锌[J].人工晶体学报,2000(01):30-33. |
| [3] | 荣利霞;李琦;李蓉萍 .真空蒸发制备ZnS薄膜及性能研究[J].内蒙古大学学报,1999,30(04):454-457. |
| [4] | 柳兆洪.溅射法制备硫化锌薄膜的探索[J].厦门大学学报,1997(01):52. |
| [5] | G.A.Domrachev;L.V.Zav'yalova;G.S.Svechnikov;O.N.Suvorova;A.V.Khanova;E.A.Shchupak;L.A.Yarosh .Samarium Dithiocarbamates as Precursors for Deposition of SmS Films[J].Russian Journal of General Chemistry,2003(4):560-565. |
| [6] | Tanemura S;Miao L;Koide S;Mori Y;Jin P;Terai A;Nabatova-Gabain N .Optical properties of metal and semiconductor SmS thin films fabricated by rf/dc dual magnetron sputtering[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2004(1/4):360-366. |
| [7] | 薛建强,龚跃球,刘孝明,徐慢.旋转涂覆法制备硫化砷玻璃薄膜及其光学性质的研究[J].玻璃与搪瓷,2003(05):18-21. |
| [8] | 杜金会,于振瑞,王旭艳,张加友,贾小东,郭淑华.电沉积法制备CoS薄膜[J].光电子·激光,2002(12):1215-1218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%