采用分步固相法合成ZrW2O8粉体,并制备出ZrW2OB/ZrO2(Al2O3)复合材料.所制备的复合材料呈近零膨胀特性,其热膨胀系数为0.48×10-6K-1.Al2O3的添加,生成新相Al2(WO4)3,提高了复合材料的致密度,而对其近零膨胀影响不大.ZrW2O8,ZrO2复合材料的导热系数为1.42 W·(m·K)-1.体积电阻率测试结果表明,在200℃以下,复合材料呈良好的绝缘性能;在200℃以上,复合材料的体积电阻率随着温度的升高而降低.
参考文献
| [1] | Barrera G D;Bruno J A O;Barron T H K et al.[J].Journal of Physics:Condensed Matter,2005,17:R217. |
| [2] | Mary T A et al.[J].Science,1996,272(05):90. |
| [3] | Evans JSO;Jorgensen JD;Short S .Compressibility, Phase Transitions, and Oxygen Migration in Zirconium Tungstate, ZrW2O8[J].Science,1997(5296):61-65. |
| [4] | 杨新波,程晓农,严学华,付廷波.负热膨胀材料ZrW2O8及其复合材料研究进展[J].材料科学与工程学报,2007(01):159-163. |
| [5] | Chang L L Y;Scrober M G;Phillips B .[J].Journal of the American Ceramic Society,1967,50:210. |
| [6] | 屈展;杨新波;程晓农.[J].机械工程材料,2007 |
| [7] | Imanaka N.;Adachi G.;Dabkowska H.;Dabkowski A.;Hiraiwa M. .Thermal contraction behavior in Al-2(WO4)(3) single crystal[J].Journal of Crystal Growth,2000(1/2):176-179. |
| [8] | Stevens R;Linford J;Woodfield B F et al.[J].Journal of Chemical Thermodynamics,2003,35:919. |
| [9] | Celik E;Islamoglu Y;Akin Y et al.[J].Materials & Design,2003,24(07):543. |
| [10] | Hashimoto T;Kuwahara J;Yoshida T et al.[J].Solid State Communications,2004,131:217. |
| [11] | Evans J S O et al.[J].Chemistry of Materials,1996,8:2809. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%