The mechanical properties, corrosion resistance and microstructures of high performance steel （HPS） was investigated by tensile testing machine, Charpy V-Notch （CVN） testing machine, cyclic immersion corrosion tester, XRD, optical microscopy （OM）, scanning electron microscopy （SEM）, and electron probe micro-analyzer （EPMA）. The results showed that significant differences existed in the tensile strength, yield strength and impact toughness between HPS and PCS. After 72 h cyclic immersion accelerated corrosion test, the inner rust layer on HPS was com- posed of a-FeOOH phase and denser than that on PCS that was a mixture of a-FeOOH and Fe3 04. The rust formed on HPS provides better protection and HPS has lower corrosion rates than PCS. Copper and chromium in HPS en- rich in the rust layer and enhance the compactness of the rust layer. Based on the results of the accelerated corrosion tests and rust layer analysis, the roles of Cu and Cr against corrosion are discussed, providing HPS with chemical specification which has been industrially successful to produce weathering steel for bridge structure.
参考文献
| [1] | Stratmann M .On the Atmospheric Corrosion of Metals Which Are Covered With Thin Electrolyte Layers--II Experimental Results[J].Corrosion Science,1990,30:697. |
| [2] | Townsend H E .Effects of Alloying Elements on the Corrosion Resistance of Steel in Industrial Environments[J].Corrosion,2001,57(06):497. |
| [3] | Misawa T;Asami K;Hashimoto K et al.The Mechanism of Atmospheric Rusting and the Protective Amorphous Rust on Low Alloy Steel[J].Corrosion Science,1974,14(04):279. |
| [4] | Choi Y S;Shim J J;Kim J K .Corrosion Behaviour of Low Al- loy Steels Containing Cr,Co and W in Synthetie Potable Water[J].Materials Seienee and Engineering,2004,385A(11):148. |
| [5] | Q.X. Li;Z.Y. Wang;W. Han;E.H. Han .Characterization of the rust formed on weathering steel exposed to Qinghai salt lake atmosphere[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(2):365-371. |
| [6] | Hara S;Kamimura T;Miyuki H et al.Taxonomy for Protec- tive Ability of Rust Layer Using Its Composition Formed on Weathering Steel Bridge[J].Corrosion Science,2007,49(03):1131. |
| [7] | T. Kamimura;S. Hara;H. Miyuki;M. Yamashita;H. Uchida .Composition and protective ability of rust layer formed on weathering steel exposed to various environments[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(9):2799-2812. |
| [8] | Matsushima I;Ueno T .On the Protective Nature of Atmos- phere Rust on Low-Alloy Steel[J].Corrosion Science,1971,11(03):129. |
| [9] | Misawa T;Kyuno T;Suetaka W et al.The Mechanism of Atmospheric Rusting and the Effect of Cu and P on the Rust Formation of Low Alloy Steels[J].Corrosion Science,1975,11:35. |
| [10] | Yamashita M;Miyuki H;Matsuda Y et al.The Long Term Growth of the Protective Rust Layer Formed on Weathering Steel by Atmospheric Corrosion During a Quarter of a Centu- ry[J].Corrosion Science,1994,36(02):283. |
| [11] | Yamashita M;Shimizu T;Konishi H et al.Structure and Protective Performance of Atmospheric Corrosion Product of Fe-Cr Alloy Film Analyzed hy MOsshauer Spectroscopy and With Synchrotron Radiation X-rays[J].Corrosion Science,2003,45(02):381. |
| [12] | Nishimura T;Katayama H;Noda K et al.Effect of Co and Ni on the Corrosion Behavior of Low Alloy Steels in Wet/Dry Environments[J].Corrosion Science,2000,42(09):1611. |
| [13] | Nishimura T;Kodama T .Clarification of Chemical State for Alloying Elements in Iron Rust Using a Binary-Phase Poten- tial-pH Diagram and Physical Analyses[J].Corrosion Sci- ence,2003,45(05):1073. |
| [14] | Nishimura T .Rust Formation and Corrosion Performance of Si and A1-Bearing Ultrafine Grained Weathering Steel[J].Corrosion Science,2008,50(05):1306. |
| [15] | K.Y. Kim;Y.H. Hwang;J.Y. Yoo .Effect of Silicon Content on the Corrosion Properties of Calcium-Modified Weathering Steel in a Chloride Environment[J].Corrosion: The Journal of Science and Engineering,2002(7):570-583. |
| [16] | Katsuhiko Asami;Michio Kikuchi .Characterization of Rust Layers on Weathering Steels Air-exposed for a Long Period[J].日本金属学会誌,2002(6):649-656. |
| [17] | Chen Y Y;Tzeng H J;Wei L I et al.Corrosion Resistance and Mechanical Properties of Low-Alloy Steels Under Atmos- pheric Conditions[J].Corrosion Science,2005,47(04):1001. |
| [18] | Asami K;Kikuchi M .In-Depth Distribution of Rusts on a Plain Carbon Steel and Weathering Steels Exposed to Coastal- Industrial Atmosphere for 17 Years[J].Corrosion Science,45(11):2671. |
| [19] | Yamashita M;Miyuki H;Matsuda Y et al.The Long Term Growth of the Protective Rust Layer Formed on Weathering Steel by Atmospheric Corrosion During a Quarter of a Centu- ry[J].Corrosion Science,1994,36(02):283. |
| [20] | Stratmann M;Bohnenkamp K;Ramchandran T .The Influ- ence of Copper Upon the Atmospheric Corrosion of Iron[J].Corrosion Science,1987,27(09):905. |
| [21] | Zhang QC.;Wu JS.;Wang JJ.;Zheng WL.;Chen JG.;Li AB. .Corrosion behavior of weathering steel in marine atmosphere[J].Materials Chemistry and Physics,2003(2):603-608. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%