综述了目前改善Al_2O_3-C耐火材料抗氧化性的三种方法:添加抗氧化剂法、浸渍氧化抑制剂法和表面涂层法;分析了常用抗氧化添加剂在Al_2O_3-C耐火材料中作用机理,展望了提高Al_2O_3-C耐火材料抗氧化性的研究方向.
In this paper,three technologies for improving the oxidation resistance of Al_2O_3-C refractories such as adding antioxidants,surface soaking and coating were reviewed.The role of additives in oxidation resistance of the refractories was analyzed.The development direction for improving the oxidation resist-ante of Al_2O_3-C refractories was prospected.
参考文献
| [1] | 马北越,于景坤,孙勇.ZrO_2-SiC复合材料的合成及其添加对Al_2O_3-C质耐火材料抗氧化性能的影响[J].金属学报,2007,43(10):1059. |
| [2] | Zhang S,Lee W E.Influence of additives on corrosion and cor-roded microstructures of MgO-C refractories[J].J Eur Ceram SOe,2001,21(13):2393. |
| [3] | 于景坤.含碳耐火材料的发展及应用[J].耐火材料,2006,40:164. |
| [4] | He Z Y,Peng X Y,Liu K O,et al.Effect of B_4C on oxidation resistance of low carbon Mgo-C materials[J].China's Refrac-tories,2007,16(4):21. |
| [5] | Chen M,Song Y L,Yu J K.Oxidation protection of Mgo-CaO-C refractories by addition of CaB_6[J].China's Refractories,2007,16(suppl.):134. |
| [6] | Chen M,Wang N,Yu J K,et al.Oxidation pmtection of CaO-ZrO_2-C refractories by addition of SiC[J].Ceramics Interna-tional,2007,33(8):1585. |
| [7] | 朱强,孙勇,于景坤,等.SiC-Al_2O_3复合粉体的合成以及在低碳镁碳砖中的应用[J].材料与冶金学报,2008,7(2):118. |
| [8] | Yu J K,Hiragushi K.Synthesis of Al_2O_3-SiC composite from pyrophyllite and clay and its application in carbon-containing refractories[J].Taikabutau,1998,50(7):375. |
| [9] | 田守信,陈肇友.添加物对Al_2O_3-C制品性能的影响[J].耐火材料,1988,22(4):14. |
| [10] | 侯谨,宋希文,孙加林,等.Mn对Al_2O_3-ZrO_2-C耐火材料抗氧化性能影响[J].耐火材料,2004,38(4):252. |
| [11] | 郭贵宝,宋希文,赵文广,等.添加锰粉对铝碳耐火材料抗氧化性的影响[J].包头钢铁学院学报,2004,23(2):118. |
| [12] | Li Y Q,Ke C M,Li Y S,et al.Effect of metallic Zn powder on oxidation of Al_2O_3-C refractories[J].China's Refractories,2006,15(4):29. |
| [13] | 孙勇.添加剂对铝碳质耐火材料性能的影响[D].沈阳:东北大学,2006.13. |
| [14] | 岳昌盛,叶方保,李庭寿.等.加入β-SiAlON对铝碳质材料性能的影响[J].耐火材料,2006,40(6):440. |
| [15] | 徐国涛,杨熹文,薛启文,等.氮化硅对烧成铝炭耐火材料的性能影响[J].硅酸盐通报,1999,18(5):18. |
| [16] | 郭巍,安胜利.二茂铁的加入对铝碳耐火材料性能的影响[J].硅酸盐通报,2007,26(5):1011. |
| [17] | 程秀梅译.含碳耐火材料中添加ZrB_2的性状和效果[J].国外耐火材料,1994(11):52. |
| [18] | 于景坤,戴文斌,戴淑平.赛隆-碳化硅系复合材料的合成及其应用[J].东北大学学报(自然科学版),2003,24(9):824. |
| [19] | Ma B Y,Yu J K,Sun Y,et al.Influences of ZrO_2-SiC compes-ite powder and commercial SiC on properties of Al_2O_3-C re-fraetories[J].China's refractories,2008,17(3):18. |
| [20] | 山口明良.碳复合耐火材料[J].耐火材料,1994,28(3):128. |
| [21] | Yang X F,Wang J X,Y B.Influences of ultra-fine B_4C and nano-SiO_2 on the properties of alumina-graphite refractories[J].China's Refractories,2004,13(4):21. |
| [22] | Yamaguchi A.Thermolchemical analysis for reaction process of aluminium and aluminium-compouds in carbon-containing re-fractories[J].Taikabutsu Overseas,1987,7(2):11. |
| [23] | 田守信,陈肇友.含炭制品中β-SiC与Al_4C_3的形成反应[J].耐火材料,1989,23(2):1. |
| [24] | 张伟刚,成会明,沈祖洪,等.炭材料抗氧化研究进展-I.实现炭材料抗氧化的主要途径[J].炭素,1997(2):1. |
| [25] | 李新健,柯昌明,李楠.含碳耐火材料的防氧化方法[J].耐火材料,2006,40(2):133. |
| [26] | 韩文瑞,周川生.铝碳耐火制品防氧化涂料的研制与使用[J].耐火材料,1991,25(3):168. |
| [27] | 刘开琪.含炭耐火材料抗氧化涂料的配制及抗氧化机理[J].耐火材料,2000,34(1):20. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%