建立了含孔复合材料层合板的三维有限元模型,以二维Zinovie理论为基础,结合改进的三维Hashin准则,对二维Zinoviev理论进行了简化和拓展,提出了适用于三维模型的刚度退化方案,完成了对层合板的渐进失效分析.从纤维失效、基体失效、分层失效三个方面讨论了层合板在拉伸载荷作用下的失效过程,并预测了层合板的拉伸极限强度及破坏模式.数值模拟结果与试验基本吻合,验证了所提出退化模型的正确性.
参考文献
| [1] | M.J. Hinton;A.S. Kaddour;P.D. Soden.A comparison of the predictive capabilities of current failure theories for composite laminates, judged against experimental evidence[J].Composites science and technology,200212/13(12/13):1725-1797. |
| [2] | P.D. Soden;A.S. Kaddour;M.J. Hinton.Recommendations for designers and researchers resulting from the world-wide failure exercise[J].Composites science and technology,20043/4(3/4):589-604. |
| [3] | 黄争鸣;张华山.纤维增强复合材料强度理论的研究现状与发展趋势--"破坏分析奥运会"评估综述[J].力学进展,2007(1):80-98. |
| [4] | P. P. Camanho;F. L. Matthews.A progressive damage model for mechanically fastened joints in composite laminates[J].Journal of Composite Materials,199924(24):2248-2280. |
| [5] | 姚辽军;赵美英;周银华.不同孔径复合材料层合板应变集中及失效强度分析[J].机械科学与技术,2011(5):761-764. |
| [6] | 鲁国富;刘勇;张呈林.含缺口复合材料层合板的三维有限元失效分析[J].力学季刊,2008(2):259-265. |
| [7] | Peter A. Zinoviev;Olga V. Lebedeva;Ludmilla P. Tairova.A coupled analysis of experimental and theoretical results on the deformation and failure of composite laminates under a state of plane stress[J].Composites science and technology,200212/13(12/13):1711-1723. |
| [8] | 史晓辉;陈秀华;汪海.基于简化Zinoviev力学模型的复合材料层压板失效分析[J].上海交通大学学报,2013(8):1210-1216. |
| [9] | 鲁国富;刘勇;张呈林.含孔复合材料层合板轴向拉伸三维有限元渐进失效分析[J].南京航空航天大学学报,2009(1):41-47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%