采用自制的磷腈单体六（烯丙氧基）环三磷腈（HACP）对不饱和聚酯树脂进行阻燃改性，用红外光谱、热重分析、极限氧指数与扫描电子显微镜测试表征分析了HACP的加入对树脂的结构、热稳定性及阻燃性的影响。结果表明：当HACP的质量分数超过10%时，HACP分子结构中的6个不饱和键不能完全参与固化反应；当HACP质量分数达到20%时，树脂的燃烧等级达到V-0，极限氧指数（LOI）为30.2%，在空气中500℃时残留率提高至30%。
The unsaturated polyester resin was modified by self-made phosphazene monomer hexallyloxycy-clophosphazene(HACP), and the effect of the addition of HACP on the structure, thermal stability, and flame retardancy of the resin was analyzed by FT-IR, TG, limited oxygen index, and SEM. The results show that when the mass fraction of HACP is more than10%, the six unsaturated bonds in HACP can not involve curing reaction completely. When the mass fraction of HACP is 20%, the flammability grade of the cured resin reaches V-0, the limiting oxygen index value is 30.2%, and the residual mass rate at 500℃increases to 30%.
参考文献
| [1] | 齐双春,兰丽琴,张彦,程海涛.近年来阻燃不饱和聚酯树脂的研究进展[J].热固性树脂,2011(02):55-59. |
| [2] | 祝晚华,刘琦焕,范春娟.不饱和聚酯树脂改性研究新进展[J].绝缘材料,2011(02):34-38. |
| [3] | 黄君仪. DOPO衍生物阻燃不饱和聚酯树脂的研究[D]. 广州:华南理工大学,2010.,2010. |
| [4] | 唐皓,郭金龙.氢氧化镁与氢氧化铝阻燃剂对不饱和聚酯树脂阻燃性能影响的研究[J].消防技术与产品信息,2009(09):49-52. |
| [5] | 张秀成,王玉峰,李斌,于耸,林茂青.反应型阻燃不饱和聚酯树脂[J].东北林业大学学报,2002(06):61-64. |
| [6] | 汪关才,卢忠远,胡小平,宋丽贤.磷钼钨杂多酸铵的合成、表征及其阻燃、抑烟性能研究[J].功能材料,2008(02):307-310. |
| [7] | 王钧,傅杰,孟红杰. 反应型阻燃不饱和聚酯树脂合成及性能研究[J]. 纤维复合材料,1996(3):11-14.,1996. |
| [8] | 邵亚婷,马庆柯,黄杰,唐安斌.环境友好型无卤阻燃苯并（噁）嗪树脂玻璃布层压板的研制[J].绝缘材料,2011(02):1-4,8. |
| [9] | 颜红侠,杨青芳,魏斌.催化合成六氯环三磷腈[J].氯碱工业,2000(08):27-28. |
| [10] | Kuan J F, Lin K F . Synthesis of Hexa-allylami no-cyclotripha-zene as a Reactive Fire Retardant for Unsaturated Polyes-ters[J].Journal of Applied Polymer Science,2004,91(2):697-702.,2004. |
| [11] | 张靓靓,许凯,陈鸣才,曹现福,陈德宏.含磷固化剂及固化环氧树脂的合成及表征[J].石油化工,2006(08):774-777. |
| [12] | 元东海,刘洪乐,黄杰,唐安斌.环保型阻燃丙烯酸酯压敏胶的制备与性能研究[J].中国胶粘剂,2012(04):33-36. |
| [13] | 杨明山,刘阳,李林楷,丁洁.六苯氧基环三磷腈的合成及对IC封装用EMC的无卤阻燃[J].中国塑料,2009(08):35-38. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%