Liquid-phase enhanced sintering of powder metallurgy (P/M) 316L stainless steel by addition of sintering aids was studied. 2%-8% of pre-alloyed Fe-Mo-B powder with two different particle sizes was added as sintering aids, and the specimens were sintered in vacuum at 1 200-1 350 ℃. The results show that the fine Fe-Mo-B powder (5-10 μm) has stronger activated effect. The sintered density increases with the increase in sintering aid content or sintering temperature. Warm compaction has a better effect on the control of dimensional precision of compacts. The prealloyed Fe-Mo-B powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.
参考文献
| [1] | Hens K F;Weaver T;German R M .Injection Molding of Various Metals and Ceramics Using an Acetal Binder[J].Advances in Powder Metallurgy and Particulate Materials,1995,2:27. |
| [2] | 果世驹,杨霞,陈邦峰,胡学晟,魏延萍.316L不锈钢粉末温压与模壁润滑的高密度成形[J].粉末冶金技术,2005(06):403-408. |
| [3] | Rutz H G;Harejjo F G;Luk S H .Warm Compaction Offers High Density at Low Cost[J].Metal Powder Report,1994,49(09):40. |
| [4] | Xia Yang,Shiju Guo,Farid Akhtar.Lubrication effectiveness of composite lubricants during P/M electrostatic die wall lubrication and warm compaction[J].北京科技大学学报（英文版）,2006(06):528-531. |
| [5] | Reen O W .Prealloyed Stainless Steel Powder for Liquid Phase Sintering[P].US 4014680,1977-03-29. |
| [6] | Gibas T;Jaworska L .Shock-Treated Boron Nitride as a Sintering Aid for c-BN Compacting Under High Pressure[J].International Journal of Refractory Metals and Hard Materials,1997,15(1-3):57. |
| [7] | L. YANG;G. MIN;H. YU .Densification and mechanical properties of CaB_6 with nickel as a sintering aid[J].Ceramics International,2005(2):271-276. |
| [8] | Palkar V R;Purandare S C;Pinto R .Breakthrough in Densification of Ferroelectric PbTiO3 With Si as Sintering Aid[J].Materials Letters,2000,43(5-6):329. |
| [9] | German R M;Dunlap J W .Processing of Iron-Titanium Powder Mixtures by Transient Liquid Phase Sintering[J].Metallurgical and Materials Transactions,1986,17A(02):205. |
| [10] | Lee D J;German R M .Sintering Behavior of Iron-Aluminum Powder Mixes[J].International Journal of Powder Metallurgy and Powder Technology,1985,21(01):9. |
| [11] | German R M;Hwang K S;Madan D S .Analysis of Fe-Mo-B Sintered Alloys[J].Powder Metallurgy International,1987,19(02):15. |
| [12] | GUO Shi-ju;LIN Tao;LI Ming-yi .Sintering Behavior of Warm-Compacted Green Compacts[J].Powder Metallurgy Technology,1999,17(02):107. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%