通过TEM和EDS对汽车用热镀锌440MPa级高强IF钢热轧和不同退火工艺条件下的析出物的形貌、分布和成分特征进行研究,并分析了退火工艺参数对析出物的影响。结果表明,热轧和退火得到的析出物主要有TiN、NbC、TiC、Fe（Ti＋Nb）P等。退火后的析出物数量都明显多于热轧板中的析出物数量,并且随着退火温度的升高和保温时间的延长,原来粗大析出物细化、分解,而原来细小析出物得以粗化、长大。
The micrographs, distribution and chemical compositions of precipitations in hot-rolling and different annealing processes were analyzed, and the influences of annealing parameters on precipitations were also studied by TEM and EDS about galvanized 440 MPa high strength IF steel for automotive. The results show that the precipita- tions are mainly composed of TiN, NbC, TiC and Fe（Ti＋Nb）P in hot rolling and annealing. The precipitations quantity of annealed steel is more than hot rolled steel, and the original coarse precipitation are reduced and originai small precipitations are growth with the increasing of annealing temperature and holding time.
参考文献
| [1] | Kitano Fusato .New Type of IF-High Strength Steel Wich Su- perior Secondary Work Embrittlement[J].ISIJ International,2001,41(11):1042. |
| [2] | 李文彬,官军.深冲钢（IF钢）的研究与发展概况[J].冶金设备,2005(03):29-34. |
| [3] | 郝晓东,程东妹,张启富.超轻汽车车体用钢热镀锌的研究及应用现状[J].中国冶金,2006(12):5-8. |
| [4] | 景财年,王作成,韩福涛.IF钢中的析出物[J].材料导报,2005(05):50-52,64. |
| [5] | 景财年,王作成,韩福涛,衣彦宏,张文平.热轧Ti-IF钢析出物的研究[J].金属热处理,2006(01):79-82. |
| [6] | Ghosh Pampa;Ghosh Chiradeep;Ray R K .Precipitation in In- terstitial Free High Strength Steel[J].ISIJ International,2009,49(07):1080. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%