分别采用直接水热合成法和浸渍法制备了Si-MCM-41, La-Si-MCM-41和Ce-Si-MCM-41介孔材料及其负载的Pt催化剂. 小角X射线衍射、氮气吸附和扩展X射线精细结构分析表明, La和Ce元素进入了MCM-41分子筛的骨架结构. NH3程序升温脱附测试未检测到含La和Ce样品表面的酸性. 所制备的催化剂具有较高的三氯乙烯催化燃烧活性及生成CO2和HCl的选择性.
参考文献
[1] | Davy C W .[J].Environmental International,2004,30(02):219. |
[2] | Quaβ U;Fermann M;Br(o)ker G .[J].Chemosphere,2004,54(09):1319. |
[3] | Spivey J J .[J].Industrial and Engineering Chemistry Research,1987,26(11):2165. |
[4] | Hutchings G J;Taylor S H .[J].Catalysis Today,1999,49(1-3):105. |
[5] | Minicò S;Scirè S;Crisafulli C;Maggiore R Galvagno S .[J].Applied Catalysis B:Environmental,2000,28(3-4):245. |
[6] | Van der Avert P;Weckhuysen B M .[J].Angewandte Chemie International Edition,2002,41(24):4730. |
[7] | Weckhuysen B;Schoonheydt R;Van der Avert P .[P].WO 03057318.A1,2003. |
[8] | Van der Avert P;Podkolzin S G;Manoilova O;de Winne H Weckhuysen B M .[J].Chemistry-A European Journal,2004,10(07):1637. |
[9] | Van der Avert P;Weckhuysen BM .Low-temperature catalytic destruction of CCl4, CHCl3 and CH2Cl2 over basic oxides[J].Physical chemistry chemical physics: PCCP,2004(22):5256-5262. |
[10] | Aranzabal A;Ayastuy-Arizti J L;González-Marcos J A;González-Velasco J R .[J].Journal of Catalysis,2003,214(01):130. |
[11] | López-Fonseca R;de Rivas B;Gutiérrez-Ortiz J I;Aranzabal A González-Velasco J R .[J].Applied Catalysis B:Environmental,2003,41(1-2):31. |
[12] | López-Fonseca R;Gutiérrez-Ortiz J I;González-Velasco J R .[J].Applied Catalysis A:General,2004,271(1-2):39. |
[13] | Zhou K B;Wang X;Sun X M;Peng Q Li Y D .[J].Journal of Catalysis,2005,229(01):206. |
[14] | Ho C;Yu J C;Kwong T;Mak A C Lai S .[J].Chemistry of Materials,2005(17):4514. |
[15] | Groppi G;Cristiani C;Lietti L;Ramella C Valentini M Forzatti P .[J].Catalysis Today,1999,50(02):399. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%