研究了海水中碳钢7周内短期腐蚀行为的电化学测试结果(包括极化曲线、线性极化法、电化学阻抗技术和恒电位阶跃法)的可靠性.结果表明,碳钢在海水中小于2个月的短期浸泡条件下,电化学方法和失重法测定的腐蚀速度均随时间逐渐减小,变化趋势相同,数值基本一致.这表明短期浸泡碳钢表面生成的腐蚀产物虽然阻碍了溶解氧的扩散,降低了腐蚀速度,但没有参加测试过程中的电化学反应.在各种电化学方法中,线性极化法和电化学阻抗技术测定的腐蚀速度与失重法最为接近,误差小于5%,可以用于2个月内短期海水浸泡碳钢的腐蚀速度监测和腐蚀行为评价.
参考文献
| [1] | Andrade C,Keddam M,N6voa X R,et al.Electrochemical behaviour of steel rebars in concrete:influence of environmental factors and cement chemistry[J].Electrochim.Acta,2001,46 (24 -25):3905. |
| [2] | Flis J,Pickering H W,Osseo-Asare K.Interpretation of impedance data for reinforcing steel in alkaline solution containing chlorides and acetates[J].Electrochim.Acta,1998,43 (12 -13):1921. |
| [3] | Videm K.Phenomena disturbing electrochemical corrosion rate measurements for steel in alkaline environments[J].Electrochim.Acta,2001,46 (24-25):3895. |
| [4] | Novak P,Mala R.Comparison of electrochemical data and mass loss corrosion rate measurements for steel reinforcements in concrete[J].European Federation of Corrosion Publications,2000,31:41. |
| [5] | 宋诗哲.腐蚀电化学研究方法[M].北京,化学工业出版社,1988:10. |
| [6] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004:161. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%