阐述了近期对于快速热氧老化的评价方法,采用热重点斜法和改进的Kinssinger方法计算改性聚芳醚的氧化活化能,同时展开低温常规长期热氧老化试验,比较快速评价方法间和常规热氧老化试验方法的差异,通过数据分析可以发现常规老化活化能与改良Kinssinger方法推导的活化能之间存在比较好的对应关系.
参考文献
| [1] | G. C. Montanari;G. Mazzanti;L. Simoni .Progress in electrothermal life modeling of electrical insulation during the last decades[J].IEEE transactions on dielectrics and electrical insulation: A publication of the IEEE Dielectrics and Electrical Insulation Society,2002(5):730-745. |
| [2] | Hondred, P.R.;Bowler, N.;Kessler, M.R. .Electrothermal lifetime prediction of polyimide wire insulation with application to aircraft[J].Journal of Applied Polymer Science,2013(3):1639-1644. |
| [3] | Maxwell AS;Broughton WR .Review of accelerated ageing methods and lifetime prediction techniques for polymer materials NPL Report DEPC MPR016[R]. |
| [4] | 郭英军;孙丽华 .电缆热老化使用寿命预测[J].河北大学学报,2007,28(1):34-36. |
| [5] | 张盈锁,韩晔.高分子材料快速热老化试验方法与化学动力学[J].合成材料老化与应用,1998(04):25. |
| [6] | Montsinger VM .Loading transformers by temperature[J].AIEE Trans,1948,67:113-122. |
| [7] | ASNI/UL746B Standard for safty for polymeric materials-long term property Evaluation[S].,2010. |
| [8] | Guidelines for application of analytical test methods for endurance testing of electrical materials IEC 1026[R].,1991. |
| [9] | 张盈锁 .热重点斜法的优点及联合验证[J].玻璃钢,1992,2:15-19. |
| [10] | JB 1544-1999.电气绝缘浸渍漆和漆布快速热老化试验方法——热重点斜法[S]. |
| [11] | Dobkowski Z .lifetime prediction for polymers via the temperature of initial decomposition[J].Journal of Thermal Analysis,1997,48:1393-1400. |
| [12] | Budrugeac P .comments lifetime prediction for polymers via the temperature of initial decomposition[J].Journal of Thermal Analysis and Calorimery,2001,65:309-312. |
| [13] | 李虹;于龙英.中小电机用F级绝缘浸渍漆耐热性评定[J].绝缘材料通讯,1995(2):8-13. |
| [14] | 罗传勇.电气绝缘材料标准使用过程中存在的问题和对策[J].绝缘材料,2001(02):24-28. |
| [15] | PR.Hondred.Degradation kinetics of polyimide film[J].High Performance Polymers,2011:337-342. |
| [16] | KT.Gillen .Evidence of non-Arrhenius behaviour from laboratory aging and 24-year field aging of polychloroprene rubber materials[J].Polymer Degradation andStability,2005,87:57-57. |
| [17] | S.K.Singh .Life prediction of composite materials subjected to long term mechanical environmental loading condition[D].The University of Alabama,2010. |
| [18] | J.D.Peterson .Kinetica of the thermal and thermo oxidative degradation of PS PE and PP[J].Macromolecular Chemistry and Physics,2001,202:775-784. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%