以可溶性锆盐(ZrOCl2·8H2O)-十六烷基三甲基溴化铵(CTAB)-正丁醇(C4H10O2)-环己烷(C6H12)组成的微乳液体系为基础、氨水作沉淀剂,在微乳区反应,经过洗涤、焙烧等工序,制备得到粒径10～40nm、形貌可控、分散性良好的ZrO2粉体.通过扫描电镜(SEM)、热分析仪(TG-DSC)以及X射线衍射分析对粉体进行表征,得到了晶相随焙烧温度的变化规律,并通过激光粒度仪以及Scherrer公式计算出粉体的粒度,从而得出粉体的粒度随浓度、溶水量以及焙烧温度的变化规律.
ZrO2 powder of 10～40nm is prepared,which is morphology control and good dispersal though the response based on the microemulsion system which is composed of soluble zirconium salt(ZrOCl2·8H2O)-the hexadecyl trimethyl ammonium bromide(CTAB)-the normal butyl alcohol(C4 H10O2)-the cyclohexane(C6H12) ,and precipitant made by ammonia in the district microemulsion.Then some working procedures is done,including wash,roasting and so on.In this article phase changes in different roasting temperatures are obtained by powder characterization with scanning electron microscopy (SEM),thermal analysis(TG-DSC) as well as X-ray diffraction analysis,and the powder granularity is calculated through laser granularity analyzer and Scherrer formula,so as to obtain the powder granularity role following the change of density soluble volume as well as the roasting temperature.
参考文献
| [1] | 祝威,王少君,赵玉军,杨婉,曲丰作.W/O型反相微乳法制备纳米材料及其应用[J].日用化学工业,2005(06):374-379. |
| [2] | 吴长英,王长龙,聂基兰.CTAB～n-C4H9OH/c-C6H12/H2O体系W/O微乳液稳定性研究[J].江西科学,2004(02):84-86,90. |
| [3] | 马维平,孙洪巍,苗芳,王松,胡行.十六烷基三甲基溴化铵/正丁醇/环己烷/水微乳液制备纳米粉体的研究[J].硅酸盐通报,2008(03):645-648,653. |
| [4] | 梁兵,孙小军.W/O型微乳液最大增容水量的研究[J].辽宁化工,2006(06):330-332. |
| [5] | 黄传勇,唐子龙,张中太.纳米级二氧化锆粉体合成新方法[J].硅酸盐学报,2000(01):11-14. |
| [6] | Kaliszew skim S;Heuer A H .Alcohol interaction with zirconia powders[J].American Ceramic Society,1990,73(06):1504. |
| [7] | Murakami Y;Ito M;Takasu Y .Synthesis of nobelmetal ox-ide ultrafine particle by sol-gel method[J].Hyomen Ka-gaku,1994,32(07):486. |
| [8] | 骆峰;阮建明;邹俭鹏 等.微乳液法制备氧化锆纳米粉体[J].硬质合金,2003,20(03):80. |
| [9] | 施利毅;华彬;张剑平 .微乳液的结构及其在制备超细颗粒中的应用[J].功能材料,1998,29(02):136. |
| [10] | 戴遐明,艾德生,李庆丰.纳米ZrO2粉体的热处理研究[J].中国粉体技术,2001(05):10-14. |
| [11] | 孙亚光;余丽秀 .二氧化锆制备及发展趋势[J].化工新型材料,2000,28(04):28. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%