采用T型微流体注射成型技术,以邻苯二甲酸二丁酯、液体石蜡和司班80为油相,间苯二酚/甲醛(RF)溶液为水相,经过溶胶-凝胶、溶剂交换、超临界干燥等过程制备了单分散RF气凝胶微球,并就制备过程中RF溶液与分散剂油相的选择、预聚时间、流速比、搅拌速率、固化温度等影响因素进行了初步讨论.当RF溶液质量分数为10%,60℃预聚1.5 h,间苯二酚与碳酸钠的物质的量之比为100,邻苯二甲酸二丁酯与液体石蜡的质量比为8:1,流速比控制在8～16,搅拌速率为65～90r/min,固化温度为35℃时,制备得到了RF乳液,其粒径分布系数小于2%.
Based on a novel T-shaped microfluidic device, monodisperse RF aerogel microspheres are prepared by using dibutyl phthalate,atoleine and span 80 as oil phase, RF solution as water phase, and by sol-gel, solvent exchanging and supercritical drying. The factors such as the choice of RF solution and oil, prepolymerization time, the flow rate ratio of oil to water phase, stirring rate and solidification temperature, which affect the process have been preliminarily discussed. When the polymerization reaction occur in the following conditions: RF solution is 10% ,prepolymerization time is 1. 5 hours at 60℃, the molar ratio of resorcinol to sodium carbonate is 100, the mass ratio of dibutyl phthalate to atoleine is 8,the flow rate ratio of oil to water phase is 8-16, stirring rate is 65～90r/min and solidification temperature is 35℃, the experiment has fabricated monodisperse RF aerogel microspheres, whose coefficient of variation (CV value) of all the RF droplets is below 2% .
参考文献
| [1] | 黄常刚,唐永建,王朝阳,闫红梅.间苯三酚-甲醛气凝胶及其碳气凝胶的制备与表征[J].强激光与粒子束,2006(06):949-952. |
| [2] | 侯海乾,王朝阳,唐永建,付志兵,张厚琼,刘淼,关峰,刘秀英.PS-RF双层空心微球的制备[J].强激光与粒子束,2008(03):406-408. |
| [3] | 侯海乾,王朝阳,唐永建,付志兵,关峰,刘淼.间苯二酚-甲醛气凝胶空心微球制备技术[J].强激光与粒子束,2008(07):1105-1108. |
| [4] | 侯海乾,王朝阳,唐永建,付志兵.激光聚变靶用RF空心泡沫微球的制备及研究进展[J].材料导报,2008(08):53-56. |
| [5] | 夏三宇,陈晓红,宋怀河.新型RF炭气凝胶微球的制备及结构表征[J].炭素技术,2005(06):5-8. |
| [6] | 尹强,张林,杜凯,李保荣.间苯二酚/甲醛泡沫微球制备技术[J].原子能科学技术,2005(05):470-473. |
| [7] | Xu S Q;Nie Z H;Seo M et al.Generation of monodisperse particles by using microfluidics-control over size shape and composition[J].Angewandte Chemie International Edition,2005,44:724. |
| [8] | Bruno G.De Geest;John Paul Urbanski;Todd Thorsen;Jo Demeester;Stefaan C.De Smedt .Synthesis of Monodisperse Biodegradable Microgels in Microfluidic Devices[J].Langmuir: The ACS Journal of Surfaces and Colloids,2005(23):10275-10279. |
| [9] | Yi G R;Thorsen T;IVhnoharan V N et al.Generation of uniform colloidal assemblies in soft midrofluidic devices[J].Advanced Materials,2003,15:1300. |
| [10] | Minseok Seo;Zhihong Nie;Shengqing Xu;Michelle Mok;Patrick C. Lewis .Continuous Microfluidic Reactors for polymer Particles[J].Langmuir: The ACS Journal of Surfaces and Colloids,2005(25):11614-11622. |
| [11] | Dendukuri D;Tsoi K;Hatton T A et al.Controlled synthesis of nonspherical rnicroparticles using microfluidics[J].Langmuir,2005,21:2113. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%