以X射线荧光光谱分析为手段,测试了用Bridgman方法生长的PbF:Gd晶体中Gd离子沿生长方向的分布.发现该晶体在X射线激发下的发光强度与Gd在PbF晶体中的含量变化均从结晶开始端至结晶结束端逐渐降低,表明PbF:Gd晶体的发光是不均匀的,这种不均匀性源于Gd离子在PbF晶体中的分布不均匀性.通过在PbF:Gd晶体中掺入一定量的碱金属离子,可以比较有效地改善Gd离子在PbF晶体中的不均匀分布,使晶体的发光均匀性和透光率得到明显提高,其中以Na离子的均匀化效果为最好.推测Na离子的作用是消除了PbF:Gd晶体中因Gd离子的掺杂而造成的间隙F离子,从而使晶体中的缺陷浓度大大降低.

Gd doped lead fluoride crystals were grown by modified Bridgman methods. Under X-ray excitation, their emission intensities peaked at 278nm and 312nm increase
with the doping amount of Gd3+ ions, but decrease from the beginning part to the finishing end of the crystallization along the growth direction. The concentration
of Gd3+ ions in the PbF_2 crystal, analyzed by X-ray fluorescence spectrophotometer, also decreases in the same direction as emission intensity does. The correspondence
between Gd content and luminescence intensity of PbF2:Gd crystal demonstrates that the non-uniformity of luminescence intensity results from the in-homogeneous
distribution of Gd3+ ions in the crystal. It was found that by co-doping suitable amount of alkali metal ions, such as Na+ and K+, with Gd ion into
PbF2 crystal, the difference of luminescent intensities and Gd3+ concentration from the bottom to the top of the crystal become smaller and the transmittance
is higher than that of the single doping crystal. Especially, the uniformization effect of Na+ ions is better than that of K+ ions. It shows that the role of

参考文献

[1] Anderson D F, et al. Nucl. Instruments and Methods in Physics Research, 1990, A290: 385
[2] Nikl M, Polak K. Phys. Stat. Sol., 1990(a), 117: k89--k92.
[3] Lecoq P, Schusskler M. Nucl. Instruments and Methods in Physics Research, 1992, A315: 337--443.
[4] Anderson D F, et al. Nucl. Instruments and Methods in Physics Research, 1994, A342: 473.
[5] 沈定中, 刘建成, 等(SHEN Ding-Zhong, et al). 无机材料学报(Journal of Inorganic Materials), 1995, 10 (1) : 11--16.
[6] 沈定中, 刘建成, 等. 中国科学(E辑),1998, 28 (1): 46--50.
[7] Blasse G, Sytsma J. Chemical Physics Letters, 1989, 155 (1): 64--68.
[8] 洪广言. 人工晶体学报,1995, 24 (2): 92--94.
[9] Kirikova N Yu. SCINT’95, Inorganic Scintillators and Their Applications, Delft, the Netherlands, Aug.28-Sept. 1995: 196--198.
[10] Chernyshev V A, et al. Appl. Magn. Reson, 1998, 14: 37.
[11] Hull S, et al. J. Phys.: Condens. Matter, 1998, 10: 8429.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%