The erosion behavior of a nanocomposite W-Cu material under arc breakdown was investigated. The arc erosion rates of the material were determined, and the eroded surfaces and arc erosion mechanisms were studied by scanning electron microscopy. It is concluded that the nanocomposite W-Cu electrical contact material shows a characteristic of spreading arcs. The arc breakdown of a commercially used W-Cu alloy was limited in a few areas, and its average arc erosion rate is twice as large as that of the former. Furthermore, it is also proved that the arc extinction ability and arc stability of the nanocomposite W-Cu material are excellent, and melting is the major failure modality in the make-and-break operation of arcs.
参考文献
| [1] | G. G. Lee;G. H. Ha;B. K. Kim .Synthesis of high density ultrafine W/Cu composite alloy by mechano-thermochemical process[J].Powder Metallurgy,2000(1):79-82. |
| [2] | Schulman M B;Slade P G;Loud L D;Wangpei Li .Influence of contact geometry and current on effective erosion of Cu-Cr,Ag-OWC,Ag-Cr vacuum contact materials[J].IEEE Transactions on Components Packaging and Manufacturing Technology,1999,22(03):405. |
| [3] | Kecskes L J;Trexler M D;Klotz B R;Choand K C Dowding R J .Densification and structural change of mechanically alloyed W-Cu composites[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2001,32A:2885. |
| [4] | Ying D Y;Zhang D L .Effect of high energy ball milling on solid state reactions in Al-25at %Ni powders[J].Mater Sci Technol,2001,17:815. |
| [5] | Bondarenko G G;Udris Y Y;Yakushin V L .On behavior of W-Cu composition as a candidate divertor material under irradiation by high intensive hydrogen plasma[J].Fusion Engineering and Design,2000,51-52:81. |
| [6] | Thomas B;Walter K V;Roland M;Sacegr K E .On the application of W/Cu materials in the fields of power engineering and plasm technology[J].IEEE Transactions,1991,14:8. |
| [7] | 陈文革,丁秉钧,张晖.机械合金化制备的纳米晶W-Cu电触头材料[J].中国有色金属学报,2002(06):1224-1228. |
| [8] | Liu P;Bahadur S;Verhoeven J D;Gibson E D Kristiansen M Donaldson A .Are erosion behavior of Cu-15%Nb and Cu-15%Cr in situ composites[J].Wear,1997,203:36. |
| [9] | Ding B J;Yang Z M;Wang X F .Influence of microstructure on dielectric strength of CuCr contact materials in a vacuum[J].IEEE Transactions on Components Packaging and Manufacturing Technology,1996,19:76. |
| [10] | Paul G. Slade;Wangpei Li;Leslie D. Loud;Richard E. Haskins Jr. .The unusual electrical erosion of high tungsten content, tungsten copper contacts switching load current in vacuum[J].IEEE transactions on components and packaging technologies: A publication of the IEEE Components, Packaging, and Manufacturing Technology Society,2001(3):320-330. |
| [11] | Fursey GN. .Field emission in vacuum micro-electronics[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):113-134. |
| [12] | Farrall GA .Electrical breakdown in vacuum[J].IEEE Transactions on Electrical Insulation,1985,20(05):815. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%