EFFECT OF MICROSTRUCTURES OF HIGH STRENGTH STEEL ON SUSCEPTIBILITY OF CADMIUM EMBRITTLEMENT

金属学报(英文版), 1989, 2(5): 343-347.

EFFECT OF MICROSTRUCTURES OF HIGH STRENGTH STEEL ON SUSCEPTIBILITY OF CADMIUM EMBRITTLEMENT

TANG Zhizhong LIU Minzhi Chengdu University of Science and Technology , Chengdu , ChinaXIAO Yaotian Institute of Metal Research , Academia Sinica , Shenyang , China Dept.of Metal Materials , Chengdu University of Science and Technology , Chengdu , China

Keywords： steel 30CrMnSiNi2A , null , null

The effect of different microstructures of steel 30CrMnSiNi2A on the susceptibility of cadmium embrittlement has been studied and compared under the unique yield strength level. The results show that the tempered martensite exhibits the maximum susceptibility to cadmium embrittlement,while the lower bainite shows the minimum susceptibility.The mixed microstructure of the above two has a susceptibility in between.

参考文献

[1]
[2]
[3]

上一张下一张

PDF下载
导出引用
下载XML
收藏文章

计量

下载量()
访问量()

作者相关

在本站搜索
TANG Zhizhong LIU Minzhi Chengdu University of Science and Technology Chengdu ChinaXIAO Yaotian Institute of Metal Research Academia Sinica Shenyang China Dept.of Metal Materials Chengdu University of Science and Technology Chengdu China
在百度学术搜索
TANG Zhizhong LIU Minzhi Chengdu University of Science and Technology Chengdu ChinaXIAO Yaotian Institute of Metal Research Academia Sinica Shenyang China Dept.of Metal Materials Chengdu University of Science and Technology Chengdu China
在万方数据库搜索
TANG Zhizhong LIU Minzhi Chengdu University of Science and Technology Chengdu ChinaXIAO Yaotian Institute of Metal Research Academia Sinica Shenyang China Dept.of Metal Materials Chengdu University of Science and Technology Chengdu China
在CNKI搜索
TANG Zhizhong LIU Minzhi Chengdu University of Science and Technology Chengdu ChinaXIAO Yaotian Institute of Metal Research Academia Sinica Shenyang China Dept.of Metal Materials Chengdu University of Science and Technology Chengdu China

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

EFFECT OF MICROSTRUCTURES OF HIGH STRENGTH STEEL ON SUSCEPTIBILITY OF CADMIUM EMBRITTLEMENT

参考文献