通过热轧试验研究了3种冷却工艺对传统成分Si-Mn系热轧双相钢组织及性能的影响。试验结果表明：在3种冷却工艺条件下,试验钢的最终组织为铁素体和马氏体双相组织。当终轧后采用空冷＋超快冷的冷却工艺时,钢板的屈强比最低,伸长率和n值最大,晶粒尺寸较大,但强度相对最小;当终轧后采用层流冷却＋空冷＋超快冷的冷却工艺时,钢板的晶粒尺寸最小,强度最大;而终轧后直接采用连续的层流冷却工艺时,得到的钢板性能介于两者之间,但冷却工艺相对简单。
The effect of cooling process on microstructure and mechanical properties of Si-Mn hot-rolled dual-phase steel was investigated hy hot-rolled test. The results show that： under the condition of the three tested processes, the final microstructure of the tested steel is composed with ferrite and martensite. When using air cooling plus ul trafast cooling after finishing rolling, the yield ratio of the tested steel is minimum, and the n-value and elongation are maximum, but the grain size of ferrite is larger, and the strengthen is relative minimum; when using laminar cooling plus air cooling and ultrafast cooling after finishing roiling, the grain size of the steel is minimum, and the strengthen is maximum; when using continuous laminar cooling after finishing rolling, the property of the steel is between other two processes, but the cooling process is relative simple.
参考文献
| [1] | Takashi Furukawa;Mitsuru Tanino .Effects of Composition and Processing Factors on the Mechanical Properties of As- Hot-Rolled Dual-Phase Steels[J].Transactions of the Iron and Steel Institute of Japan,1984,24:113. |
| [2] | Tomoyoshi Okita;Yoshihiro Hosoya;Kazuhide Nakaoka.Manufacturing Process of As Hot-Rolled Dual Phase Steel[J].Tetsu To Hagane-Journal of the Iron and Steel Institute of Japan,1982(68):1313. |
| [3] | Kyung-Tae PARK;Young Kook LEE;Dong Hyuk SHIN .Fabrication of Ultrafine Grained Ferrite/Martensite Dual Phase Steel by Severe Plastic Deformation[J].ISIJ International,2005(5):750-755. |
| [4] | Se-Jong Kim;Yi-Gil Cho;Chang-Seok Oh;Dong Eun Kim;Man Been Moon;Heung Nam Han .Development Of A Dual Phase Steel Using Orthogonal Design Method[J].Materials & design,2009(4):1251-1257. |
| [5] | Ekrami A .High Temperature Mechanical Properties of Dual Phase Steels[J].Materials Letters,2005,59:2070. |
| [6] | 陈连生,狄国标,王月香,刘振宇,刘相华,何舒星.含Nb低Si-Mn热轧双相钢的工艺研究[J].轧钢,2006(03):1-3. |
| [7] | 陈良,宋平.采用控轧控冷工艺生产车轮用双相钢[J].轧钢,2005(04):66-67. |
| [8] | 唐多光;冯锋;万晓景 .载重汽车大梁用热轧双相钢板[J].钢铁,1994,29(06):48. |
| [9] | 刘彦春,董瑞峰,屈文胜,闫波,王建钢,王国栋.CSP线生产C-Mn系热轧双相钢的工业试验[J].轧钢,2006(04):1-4. |
| [10] | 狄国标,陈连生,刘振宇,赵迪,刘相华.薄板坯连铸连轧低温卷取生产双相钢的工业试验[J].钢铁,2009(06):65-68. |
| [11] | 徐海卫,杨王玥,孙祖庆.基于动态相变的细晶双相低碳钢组织控制[J].金属学报,2006(10):1101-1108. |
| [12] | Shikanai N;Kagawa H;Kurihara M .Influence of Micro- structure on Yield Behavior of Heavy Gauge High Strength Steel Plates[J].ISIJ International,1992,32(03):335. |
| [13] | 于庆波,赵贤平,孙斌,于爱民,陈波.高层建筑用钢板的屈强比[J].钢铁,2007(11):74-78,16. |
| [14] | 焦多田,蔡庆伍,武会宾.轧后冷却制度对X80级抗大变形管线钢组织和屈强比的影响[J].金属学报,2009(09):1111-1116. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%