以8mol%钇稳定化氧化锆(YSZ)为原料,以阿拉伯树胶为分散剂和粘接剂,采用改进注浆法制备出长度为226～260mm、壁厚为0.4～0.9mm的致密YSZ电解质薄管.设计并制出带有一定锥度的空芯石膏模,研究了球磨时间对成型料浆稳定性的影响,烧结温度对YSZ样品致密度的影响.研究结果表明:球磨时间在75～140min的范围内料浆的稳定性较好,随烧结温度的升高,样品的致密度提高.用这种YSZ薄管制成固体氧化物燃料电池,电池的电学性能随温度的升高而明显提高,三节电池串联的最大功率为2.2W.
参考文献
| [1] | Etsell T H;Flengas S N .[J].Chemical Reviews,1970,70(03):357-358. |
| [2] | Radford K C;Bratton R J .[J].Journal of Materials Science,1979,14:19-69. |
| [3] | Minh N Q .[J].Journal of the American Ceramic Society,1993,76(03):563-588. |
| [4] | U S Department of Energy.Office of Fossil Energy Morgantown Energy Technology Center[M].Fuel Cells A Handbook (Revision 3),1994:5-1. |
| [5] | Gibson IR.;Irvine JTS.;Dransfield GP. .Sinterability of commercial 8 mol% yttria-stabilized zirconia powders and the effect of sintered density on the ionic conductivity[J].Journal of Materials Science,1998(17):4297-4305. |
| [6] | 祝桂洪.陶瓷工艺实验[M].北京:中国建筑工业出版社,1987:48-51. |
| [7] | Joseph A Pask .[J].American Ceramic Society Bulletin,1979,58:1169. |
| [8] | 杨金龙;吴健光;黄勇 .[J].硅酸盐通报,1995,5:76-77. |
| [9] | 卢旭晨;袁启明;杨正方 .[J].中国陶瓷,1997,33(03):23. |
| [10] | 刘江 .[D].长春:吉林大学,1997. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%