Microstructure and Mechanical Properties of Magnesium Alloy AZ31B Brazed Joint Using a Zn-Mg-A1 Filler Metal

材料科学技术（英）, 2010, 26(8): 743-746.

^1, , ^2, , ^3, , ^4,

1.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

2.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

3.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

4.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

基金项目: the Beijing Municipal Education Commission(KM200710005005)

Microstructure and Mechanical Properties of Magnesium Alloy AZ31B Brazed Joint Using a Zn-Mg-A1 Filler Metal

Li Ma ^1, , Dingyong He ^2, , Xiaoyan Li ^3, , Jianmin Jiang ^4,

1.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

2.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

3.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

4.College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China

Keywords： Filler metal

In order to join the similar magnesium alloy,a novel Zn-Mg-AI filler metal was designed and applied to braze AZ31B plates by using high-frequency induction brazing technique. The microstructure,phase constitution and fracture morphology of the brazed joint were investigated. The experimental results show that MgZn2 phase in the original filler metal is completely consumed in the brazing process. Moreover,а-Mg solid solution and а-Mg+MgZn eutectoid structure formed in the brazing region due to the intensive alloying between the molten filler metal and the base metal in the brazing process. Test results indicate that the shear strength of the brazed joint is 56 MPa. The fracture morphology of the brazed joint shows intergranular fracture mode,where crack originates from the hard а-Mg+MgZn eutectoid structure.

参考文献

[1]	G.M.Xie,Z.Y.Ma,L.Geng.Effect of Y Addition on Microstructure and Mechanical Properties of Friction Stir Welded ZK60 Alloy[J].材料科学技术学报（英文版）,2009(03):351-355.
[2]	J.M.Kim,J.H. Jun,W.J. Jung.Mg-Al Alloys Manufactured by Casting and Hot Working Process[J].材料科学技术学报（英文版）,2008(01):96-98.
[3]	L. Commin;M. Dumont;J.-E. Masse .Friction stir welding of AZ31 magnesium alloy rolled sheets: Influence of processing parameters[J].Acta materialia,2009(2):326-334.
[4]	L.M. LIU;Z.D. ZHANG;G. SONG .Mechanism and Microstructure of Oxide Fluxes for Gas Tungsten Arc Welding of Magnesium Alloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2007(3):649-658.
[5]	Z.D. Zhang;L.M. Liu;Y. Shen .Mechanical properties and microstructures of a magnesium alloy gas tungsten arc welded with a cadmium chloride flux[J].Materials Characterization,2008(1):40-46.
[6]	L.M. Liu;J.H. Tan;L.M. Zhao .The relationship between microstructure and properties of Mg/Al brazed joints using Zn filler metal[J].Materials Characterization,2008(4):479-483.
[7]	L.-M. Liu;H.-Y. Wang;Z.-D. Zhang .The analysis of laser weld bonding of Al alloy to Mg alloy[J].Scripta materialia,2007(6):473-476.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Microstructure and Mechanical Properties of Magnesium Alloy AZ31B Brazed Joint Using a Zn-Mg-A1 Filler Metal

参考文献