采用泥浆喷涂工艺制备SOFC用阳极支撑YSZ电解质薄膜,首先采用模压成型工艺制窷iO-YSZ阳北极基底,通过优化泥浆制备工艺条件及喷涂条件,在NiO-YSZ阳极基底上喷涂均匀平整的YSZ电解质涂层,进一步采用共烧结工艺使YSZ电解质层致密.通过在基底中添加碳粉造孔剂,调节阳极基底的烧结收缩率与电解质层烧结收缩率一致,避免电解质涂层的开裂和变形.阳极基底中加入5wt%含量的碳粉,阳极与电解质层烧结收缩率一致.扫描电子显微镜观察电解质涂层表面形貌表明,球磨24h的泥浆喷涂的YSZ涂层较好,阳极基底与电解质膜在1400℃烧结2h,电解质膜层致密,表明通过泥浆喷涂工艺可以制备出致密电解质层.
参考文献
| [1] | SchoonmanJ;Dekker J P;Broers J W et al.Electrochemicalvapordepositionofstabilizedzirconiaandinterconnectionmaterialsforsolidoxidefueleells[J].Solid State Ionics,1991,46:299. |
| [2] | M. Lang;R. Henne;S. Schaper;G. Schiller .Development and characterization of vacuum plasma sprayed thin film solid oxide fuel cells[J].Journal of Thermal Spray Technology,2001(4):618-625. |
| [3] | 章金天;唐超群;周东祥 .YSZ薄膜Sol-gel法制备及其结构分析[J].无机材料学报,1997,12(02):200. |
| [4] | SergeRamert;Augustin McEvoy;Peter H.Spary thin-film electrolyte in anode-supported cells,joep huijsmans[A].Lucerne/Switzerland,2002 |
| [5] | MenzlerNH;Fleck R;Mertens J.Appliction of wet chemical technologies for tubular SOFCs joep huijsmans[A].Lucerne/Switzerland,2002 |
| [6] | 刘福田,李兆前,黄传真,张涛.金属陶瓷覆层材料坯体的料浆法成形工艺[J].机械工程材料,2002(09):13-16,24. |
| [7] | 阎景旺,董永来,于春英,江义.中温固体氧化物燃料电池阳极基底及负载型电解质薄膜的研制[J].无机材料学报,2001(05):804-814. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%