研究了片式BaTiO3基PTCR元件石膏模注浆成型工艺,通过控制pH值、粘合剂及分散剂的含量,获得具有较高固相比和较低粘度的浆料.在PVA和分散剂占粉料质量比分别为0.8％和0.4％且pH=9时,获得的浆料最高固相质量分数为80％(固相体积分数为55％).利用注浆成型能够通过模具尺寸及吸浆时间来控制膜厚的特点,成功制备出厚度为0.4mm且具有一定强度和密度的生坯,并考察了注浆成型瓷片的PTCR效应,且对成型过程中的一些现象作出了分析和讨论.
In order to acquire highly concentrated BaTiO3 slurry suitable for slipcasting process, the factors, that may influence the property of slurry, were investigated. The results obtained show that when pH=9 and the weight concentration of PVA and dispersant is 0.8% and 0.4% respectively, the solids loading as high as 80wt%(55vol%) can be achieved. In addition, The PTCR effect of chip PTCR formed by this slipcasting process was examined.
参考文献
| [1] | ] 西村弘治, 鹤田智#[39], 渡边浩一. 积层型PTCRサーミスタ及びそ?の制造方法. 日本, 公开专利公报, 特开平10-12404[P], 1998. [2] 黄勇, 向军辉, 谢志鹏, 等. 硅酸盐通报, 2001, 5: 22--27. [3] 胡云香, 周东祥, 龚树萍, 等. 中国陶瓷, 2001, 37 (2): 13--15. [4] 刘学建, 黄莉萍, 古宏晨, 等. 陶瓷学报, 1999, 20 (4): 230--234. [5] 浦雪琴, 朱军. 真空电子技术, 2002, 3: 48--50. [6] 华南工学院, 南京化工学院, 武汉建筑材料工业学院. 陶瓷工艺学, 北京: 中国建筑工业出版社, 1978. 87--97. [7] 向军辉, 黄勇, 谢志鹏, 等. 高技术通讯, 2002, 02: 58--61. [8] Jean J H, Wang H R. J. Am. Ceram. Soc., 2000, 83 (2): 277--280. [9] Jean J H, Wang H R. J. Am. Ceram. Soc., 1998, 81 (6): 1589--1599. [10] 李懋强(LI Mao-Qiang). 硅酸盐学报(Journal of the Chinese Ceramic Society), 2001, 29 (5): 466--470. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%