聚碳酸酯(PC)与经臭氧化处理的POE共混后,其力学性能、低温冲击性能、抗溶剂性能以及冲击性能对壁厚的依赖性显著改善.在PC中加入经120 min臭氧化处理的POE后,PC/POE(90/10)共混物的冲击强度与PC相比从24.6 kJ/m2提高到72.5 kJ/m2,低温(-20℃)冲击强度从18.8 kJ/m2提高到68.6 kJ/m2.在丙酮中浸泡4 h后,共混物的冲击强度与PC(降至3.2 kJ/m2)相比仅降至43.7 kJ/m2.未经改性处理的PC冲击强度从67.7 kJ/m2(壁厚3.2 mm)迅速下降到11.5 kJ/m2(壁厚6.4 mm);经120 min臭氧化处理,PC/POE(90/10)共混物的冲击强度从75.5 kJ/m2(壁厚3.2 mm)仅下降到58.0 kJ/m2(壁厚6.4 mm).PC/POE(90/10)共混体系的加工流变性能与PC相比也得到改善.
参考文献
| [1] | Cho K;Lee M S;Park C E .[J].POLYMER,1998,39(06):1357. |
| [2] | Moskala EJ. .A fracture mechanics approach to environmental stress cracking in poly(ethyleneterephthalate)[J].Polymer: The International Journal for the Science and Technology of Polymers,1998(3):675-680. |
| [3] | Sue H J;Huang J;Yee A F .[J].POLYMER,1992,33:4868. |
| [4] | Yang M;Zhang Z;Feng J .[J].Polymer Engineering and Science,1998,38:879. |
| [5] | Kim B K;Park S Y.[J].Journal of Polymer Engineering,1991(10):289. |
| [6] | Suzuki T;Kotaka T .[J].Polymer Journal,1983,15(01):15. |
| [7] | Li CQ.;Zhang Y.;Zhang YX.;Zhang CM. .Blends of polycarbonate and ethylene-1-octylene copolymer[J].European Polymer Journal,2003(2):305-311. |
| [8] | 李晶;吕荣侠 .[J].现代塑料加工应用,1999,11(06):1. |
| [9] | 冯继云;李松;张增民 .[J].塑料,1993,22(06):26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%