采用蒸氨均相共沉淀法,即加热含有Cu2+和WO42-的氨络合物溶液,使氨蒸发,获得沉淀物,然后对沉淀物进行煅烧、还原,最终制得了含Cu量为20%的W-Cu复合粉.对沉淀物和W-Cu复合粉的组成和粒度等进行了表征.同时对于不同温度下烧结上述W-Cu复合粉压坯所得烧结体的微结构和物理、力学性能等进行了测试分析.试验结果表明,蒸氨均相共沉淀法制备的W-Cu复合粉体具有纳米粒度和均匀的化学组成,其烧结活性高,在较低温度下烧结即可达很高的致密化程度;所得烧结体具有良好的物理、力学性能.
参考文献
[1] | Johnson J L;German R M .Advance in powder metallurgy and particulate materials[J].International Journal of Powder Metallurgy,1993,4:201-209. |
[2] | David J W;Barabash V R;Makhankov A et al.Assessment of tungsten for use in ITER plasma facing components[J].Journal of Nuclear Materials,1998,258-263:308-312. |
[3] | Sebastian KV .Properties of sintered and infiltrated tungsten-copper electrical contact material[J].International Journal of Powder Metallurgy,1981,17:297-303. |
[4] | Fecht H J .Synthesis and properties of nanocrystalline metals and alloys prepared by mechanical attrition[J].Nano-Structured Materials,1992,1:125-130. |
[5] | Kim B K;Choi C J .Fabrication of nanostructured powders by chemical processes[J].Scripta Materialia,2001,44:2161-2164. |
[6] | Gusmano G.;Polini R.;Magistris P.;Marcheselli G.;Bianco A. .Chemical synthesis and sintering behaviour of highly dispersed W/Cu composite powders[J].Journal of Materials Science,2001(4):901-907. |
[7] | G. G. Lee;G. H. Ha;B. K. Kim .Synthesis of high density ultrafine W/Cu composite alloy by mechano-thermochemical process[J].Powder Metallurgy,2000(1):79-82. |
[8] | Kim T H;Kim J H;Yu J S et al.The mechanism of hydrogen reductions synthesis of nanocomposite W-Cu powders[J].Nano-Structured Materials,1997,9:213-216. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%