采用Ti-5Al-2.5Sn ELI (TA7 ELI)洁净预合金粉末通过热等静压(HIP)致密化工艺制备TA7 ELI合金.利用粒度仪和扫描电镜等对粉末的粒径分布、形貌和化学成分进行表征.利用金相显微镜分析热等静压后TA7 ELI合金的显微组织,利用电子探针分析包套和粉末反应层的元素分布.结果表明:粉末的平均粒度约为80 μm,形貌呈球形;经1 000 ℃、130 MPa、3 h热等静压后,材料的相对密度达到理论密度的99.5%,获得平均晶粒直径约为40 μm的细小等轴晶组织;包套与TA7 ELI粉末界面反应层厚度为3～8 μm,反应层富集Al和Sn元素,Fe元素沿TA7 ELI晶界快速扩散,在界面附近呈网状分布.
参考文献
| [1] | ARZT E;ASHBY M F;EASTERLING K E .Practical applications of hot-isostatic pressing diagrams:Four case studies[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1983,14:211-221. |
| [2] | D.P. DFLO;H.R. PIEHLER .EARLY STAGE CONSOLIDATION MECHANISMS DURING HOT ISOSTATIC PRESSING OF Ti-6Al-4V POWDER COMPACTS[J].Acta materialia,1999(9):2841-2852. |
| [3] | ARZT E .The influence of an increasing particle coordination on the densification of spherical powders[J].Acta Metallurgica,1982,30:1883-1890. |
| [4] | H.V. ATKINSON;S. DAVIES .Fundamental Aspects of Hot Isostatic Pressing: An Overview[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(12):2981-3000. |
| [5] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1997:2-3. |
| [6] | LOH N L;SIA K Y .An overview of hot isostatic pressing[J].Journal of Materials Processing Technology,1992,30:45-65. |
| [7] | 黄伯云;李成功;石力开;邱冠周 左铁镛.中国工程材料大典[M].北京:化学工业出版社,2006:523-527. |
| [8] | Gerhard Wegmann;Rainer Gerling;Frank-Peter Schimansky .Temperature induced porosity in hot isostatically pressed gamma titanium aluminide alloy powders[J].Acta materialia,2003(3):741-752. |
| [9] | BESSON J;ABOUAF M .Grain growth enhancement in alumina during hot isostatic pressing[J].Acta Metallurgical Materialia,1991,39(10):2225-2234. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%