通过乙酰丙酮钇与聚碳硅烷反应,得到分子量适中(Mw=2816)、GPC曲线呈双峰分布、具有优异可纺性的新型先驱体含钇聚碳硅烷,在控制纺丝温度和压力后,得到表面光滑、无裂纹、直径为5.3 μm的原纤维.讨论了原纤维直径对纤维制备工艺及性能的影响.降低纤维直径,有利于减少纤维缺陷,提高纤维强度和柔顺性.当纤维直径为6.20 μm时,抗张强度为3.52 GPa,且随直径减小,抗张强度呈线性增长趋势,为制备新型含异质元素耐超高温SiC纤维奠定了基础.
参考文献
| [1] | Yajima S;Hayashi J;Omori M et al.[J].Nature,1976,261:683. |
| [2] | He rzog A;Thunemann M;Vogt U et al.[J].Journal of the European Ceramic Society,2005,25:187. |
| [3] | Song Y C;Feng C;Tan Z et al.[J].Journal of Materials Science Letters,1990,9:1310. |
| [4] | Song Y C;Hasegawa Y;Yang S J et al.[J].Journal of Materials Science,1988,23:1911. |
| [5] | Ishikawa T;Kohtoku Y;Kumagawa K et al.[J].Nature,1998,391:773. |
| [6] | Van Dijen F K;mayer E .[J].Journal of the European Ceramic Society,1996,16:413. |
| [7] | 岳中仁;李仍元;王平华 et al.[J].合成纤维工业,1991,14(03):29. |
| [8] | Song Y C;Feng C X;Wang J .[J].Journal of Materials Science Letters,2003,22:679. |
| [9] | 王应德;宋永才;邹治春 et al.[J].合成纤维,1997,26(06):11. |
| [10] | Yang D X;Song Y C;Man X H et al.[J].Key Engineering Materials,2007,336(02):1297. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%