研究了保持时间和应变幅对C-276合金650℃下的低周疲劳寿命的影响.测试中采用应变幅为0.3%,0.35%,0.4%,0.45%和0.5%,保持时间为0,30和60 s的梯形波轴向总应变控制疲劳实验,并利用扫描电镜(SEM)观察了合金在各实验条件下的断口特征.结果表明,在同一保持时间下,随着应变幅的增加,裂纹扩展速率增大,疲劳寿命降低.而保持时间的引入对疲劳寿命的影响则与应变幅的大小有关:在较低的应变幅(0.35%~0.4%)下,引入保持时间,造成疲劳裂纹扩展速率增大,并且有微裂纹和空洞形成,在两者的共同作用下使疲劳寿命降低;在较高的应变幅(0.45%~0.5%)下,引入保持时间,造成微裂纹和空洞的焊合,使疲劳寿命不降反升.

参考文献

[1] 程旭,刘晓晶.超临界水冷堆国内外研发现状与趋势[J].原子能科学技术,2008(02):167-172.
[2] 马雁,陆道纲,毛雪平,张立殷,蔡军.C-276合金650℃下持久抗力的显微分析[J].稀有金属材料与工程,2010(09):1571-1574.
[3] 蒋有荣.China's Nuclear Society Nuclear Material Academic Symposium(中国核学会核材料分会学术交流会论文集)[M].Beijing:Chinese Nuclear Society,2007
[4] Tarun Goswami;Hannu Hanninen .Dwell effects on high temperature fatigue behavior Part I[J].Materials & Design,2001(3):199-215.
[5] Tarun Goswami;Hannu Hanninen .Dwell effects on high temperature fatigue damage mechanisms Part II[J].Materials & Design,2001(3):217-236.
[6] 陈立佳 .Low Cycle Fatigue and Fatigue-creep nteraction Behaviour of Two Nickel Base Superalloys(种镍基高温合金低周疲劳及疲劳蠕变交互作用的研究)[D].Shenyang:Institute of Metal Research,Chinese Academy of Science,1999.
[7] Adefris N;Saxena A .[J].Engng Fatigue Fract,1996,19:401.
[8] Lu Y L;Liaw P K;Sun Y et al.[J].Acta Materialia,2007,55:767.
[9] Lu YL;Chen LJ;Liaw PK;Wang GY;Brooks CR;Thompson SA;Blust JW;Browning PF;Bhattachary AK;Aurrecoechea JM .Effects of temperature and hold time on creep-fatigue crack-growth behavior of HAYNES (R) 230 (R) alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1-2):1-10.
[10] Roy, A.K.;Chatterjee, S.;Hasan, M.H.;Pal, J.;Ma, L. .Crack-growth behavior of alloy 230 under creep-fatigue conditions[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(18/19):4830-4836.
[11] Gharad A El;Zedira H;Azari Z et al.[J].Eng Fra Mech,2006,73:750.
[12] Terry C. Totemeier;Hongbo Tian .Creep-fatigue-environment interactions in INCONEL 617[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):81-87.
[13] 廖景娱.Failure Analysis of Metal Components(金属构件失效分析)[M].北京:化学工业出版社,2003:71.
[14] Martin Bojinov;Gunilla Fabricius;Petri Kinnunen;Timo Laitinen;Kari Makela;Timo Saario;Goran Sundholm;Kirsi Yliniemi .Transpassive dissolution of Ni-Cr alloys in sulphate solutions-comparison between a model alloy and two industrial alloys[J].Electrochimica Acta,2002(11):1697-1712.
[15] Melvin F Kanninen;Popelar C H.Advanced Facture Mechanics[M].Oxford:Oxford University Press,1985:305.
[16] 张俊善.High Temperature Deformation and Fracture(材料的高温变形与断裂)[M].北京:科学出版社,2007:01.
[17] 束德林.Mechanical Properties of Engineering Materials(工程材料力学性能)[M].北京:机械工业出版社,2007:08.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%