采用放电等离子烧结技术制备了KF-Ni60B镍基自熔合金,通过硬度、密度测试,研究了烧结温度、保温时间和烧结压力对烧结体性能的影响,并对烧结工艺进行了优化.结果表明:烧结温度对该合金性能的影响最大,烧结压力和时间的影响次之;在65 MPa压力下,经870℃烧结15 min的Ni60B自熔合金性能最佳,硬度为64.22 HRC,密度为7.713 g·cm-3;烧结后的合金组织为在γ-Ni固溶体基体上均匀分布着铬、铁的碳化物、硼化物等硬质相,晶粒均匀细小.
参考文献
[1] | Huahui Chen;Caiyun Xu;Jun Chen;Huiyou Zhao;Lei Zhang;Zhenting Wang .Microstructure and phase transformation of WC/Ni60B laser cladding coatings during dry sliding wear[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2008(7/8):487-493. |
[2] | T. Gomez-del Rio;M. A. Garrido;J. E. Fernandez;M. Cadenas;J. Rodriguez .Influence of the deposition techniques on the mechanical properties and microstructure of NiCrBSi coatings[J].Journal of Materials Processing Technology,2008(1/3):304-312. |
[3] | Navas C;Colaco R;de Damborenea J;Vilar R .Abrasive wear behaviour of laser clad and flame sprayed-melted NiCrBSi coatings[J].Surface & Coatings Technology,2006(24):6854-6862. |
[4] | K. Matsugi;T. Hatayama .Impact properties of spark sintered titanium aluminides at elevated temperatures[J].Intermetallics,1999(9):1049-1057. |
[5] | Dustin M. Hulbert;Andre Anders;Joakim Andersson .A discussion on the absence of plasma in spark plasma sintering[J].Scripta materialia,2009(10):835-838. |
[6] | Mamoru Omori .Sintering, consolidation, reaction and crystal growth by the spark plasma system (SPS)[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(2):183-188. |
[7] | Anselmi-Tamburini U;Kodera Y;Gasch M;Unuvar C;Munir ZA;Ohyanagi M;Johnson SM .Synthesis and characterization of dense ultra-high temperature thermal protection materials produced by field activation through spark plasma sintering (SPS): I. Hafnium Diboride[J].Journal of Materials Science,2006(10):3097-3104. |
[8] | 文小浩,陈胜,韩小云,丁小芹,张学彬,徐金富.SPS烧结M42粉末高速钢的烧结工艺研究[J].兵器材料科学与工程,2009(04):70-74. |
[9] | 冯海波,周玉,贾德昌.放电等离子烧结技术的原理及应用[J].材料科学与工艺,2003(03):327-331. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%