液滴下金属海洋大气腐蚀是大气腐蚀的一种重要形式，对海上设施和海岸建筑物造成很大破坏，因此研究液滴腐蚀有重要意义．近年来液滴下海洋大气腐蚀的研究取得了一定的成果．大量研究表明，液滴性质对金属海洋大气腐蚀起到关键性作用，
参考文献
| [1] | 王凤平,陈华,李晓刚.盐粒沉降对Zn大气腐蚀的影响[J].J.Univ.Sci.Technol.Beijing,2002,24(4):445. |
| [2] | Prosek T, Thierry D, Taxen C, et al. Effect of cations on corrosion of zinc and carbon steel covered with chloride de- posits under atmospheric conditions[J]. Sei. Direct., 2007, 49(6): 2676. |
| [3] | Corvo F , Haces C, Betancourt N, et al. Atmospheric corrosivity in the caribbean area[J]. Corros. Sci., 1997, 39(5): 823. |
| [4] | Stratmann M, Streckel H. On the atmospheric corrosion of metals which are covered with thin electrolyte layers-I. Verification of the experimental technique[J]. Corros. Sci., 1990, 30(6,7): 681. |
| [5] | Yadav A P, Nishikata A, Tsuru T. Degradation mechanism of galvanised steel in wet-dry cyclic environment containing chloride ions[J]. Corros. Sci., 2004, 46(2): 361. |
| [6] | Muster T H, Bradbury A, Trinchi A, et al. The atmospheric corrosion of zinc: The effects of salt concentration, droplet size and droplet shape[J]. Electrochim. Acta, 2011, 56 (4): 1866. |
| [7] | Tsutsumi Y, Nishikata A, Tsuru T. Pitting corrosion mechanism of Type 304 stainless steel under a droplet of chloride solutions[J]. Corros. Sci., 2007, 49(3): 1394. |
| [8] | Maier B, Frankel G S. Pitting corrosion of bare stainless steel 304 under chloride solution droplets[J]. J. Electrochem. Soc., 2010, 157(10): C302. |
| [9] | Hastuty S, Nishikata A, Tsuru T. Pitting corrosion of type 430 stainless steel under chloride solution droplet[J]. Corros. Sci., 2010, 52(6): 2035. |
| [10] | Li S X, Hihara L H. Atmospheric corrosion initiation on steel from predeposited NaCl salt particles in high humidity atmosphereIJ]. Corros. Eng. Sci. Technol., 2010, 45(1): 49. |
| [11] | Cole I S, Azmat N S, Kanta A. What really controls the atmospheric corrosion of zinc ? Effect of marine aerosols on atmospheric corrosion of zinc[J]. Int. Mater. Rev., 2009, 54(3): 117. |
| [12] | Tan Y J. Wire beam electrode: A new tool for studying localised corrosion and other heterogeneous electrochemical processes[J]. Corros. Sci., 1999, 41 (2): 229. |
| [13] | Dubuisson E, Lavie P, Dalard F, et al. Corrosion of galvanised steel under an electrolytic drop[J]. Corros. Sci., 2007, 49(2): 910. |
| [14] | Brown P W, Masters L W. Atmospheric Corrosion[A]. New York: John Wiley &: Sons, 1982. |
| [15] | Haynie F H. Atmospheric Corrosion[M]. New York: John Wiley & Sons, 1982. |
| [16] | Svensson J E, Johansson G. A laboratory study of the effect of ozone nitrogen dioxide, and sulfar dioxide on the atmospheric corrosion of zinc[J]. J. Eleetrochem. Soc., 1993, 140(8): 2210. |
| [17] | 屈庆,严川伟等.NaCl和SO2在A3钢初期大气腐蚀中的协同效应[J].金属学报,2002,38(10):1062. |
| [18] | Dubuisson E, Lavie P, Dalard F, et al. Study of the atmospheric corrosion of galvanised steel in a micrometrie electrolytic droplet[J]. Electrochem. Commun., 2006, 8(6): 911. |
| [19] | Chen Z Y, Persson D, Leygraf C. Initial NaCl-particle induced atmospheric corrosion of zinc-Effect of CO2 and SO2[J]. Corros. Sci., 2008, 50: 111. |
| [20] | 王佳.无机盐微粒沉积和大气腐蚀的发生与发展[J].中国腐蚀与防护学报,2004,24(3):155. |
| [21] | Wang J, Tsuru T. Potential distribution and microdroplets formation on the metal with salt particle deposition[A]. The 204th Meeting of The Electrochemical Society[C]. Orlando: The Electrochemical Society, Inc. 2003, D2: 472. |
| [22] | Tsuru T, Tamiya K I, Nishikata A. Formation and growth of micro-droplets during the initial stage of atmospheric corrosion[J]. Electrochim. Acta, 2004, 49(17-18): 2709. |
| [23] | Neufeld A K, Cole I S, Bond A M, et al. The initiation mechanism of corrosion of zinc by sodium chloride particle deposition[J]. Corros. Sci., 2002, 44(3): 555. |
| [24] | Neufeld A K. Investigations using a Kelvin probe instrument and solid state electrochemical techniques: the initiation mechanism of corrosion of zinc and the solid-solid elec- trochemical transformation of CuTCNQ[D]. Melbourne: Monash University, 2003. |
| [25] | Wang J, Zhang J B. The effect of micro-droplets formation caused by the deliquescence of the deposited salt particle on atmospheric corrosion of metals[C]. Beijing: Proc. 16ICC, No. 5-B-10, 2005. |
| [26] | Zhang J B, Wang J, Wang Y H. Electrochemical investigations of micro-droplets formed on metals during the deliquescence of salt particles in atmosphere[J]. Electrochem. Commun., 2005, 7(4): 443. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%