为提高高强铝合金钨极氩弧焊的效率,以LD10铝合金为研究对象,将TiO2,SiO2作为活性剂涂敷在试件表面,采用TIG方式进行焊接.研究TiO2,SiO2作为活性剂对焊缝深宽比、显微组织和接头显微硬度的影响.结果表明:活性剂的涂敷均会使焊缝熔宽增加、熔深加大；添加SiO2活性剂焊件的焊缝和热影响区硬度低于常规焊接件,添加TiO2活性剂焊件的焊缝硬度低于常规焊接件,但TiO2活性剂焊件焊接热影响区的硬度高于常规焊接件.
参考文献
| [1] | 宋仁国.高强度铝合金的研究现状及发展趋势[J].材料导报,2000(01):20-21,34. |
| [2] | 潘志军,黎文献,马正青,谭敦强.高强铝合金的研究现状及展望[J].铝加工,2001(04):39-41. |
| [3] | 刘志华,赵兵,赵青.21世纪航天工业铝合金焊接工艺技术展望[J].导弹与航天运载技术,2002(05):63-68. |
| [4] | S. W. Shyu;H. Y. Huang;K. H. Tseng;C. P. Chou .Study of the Performance of Stainless Steel A-TIG Welds[J].Journal of Materials Engineering and Performance,2008(2):193-201. |
| [5] | Xu YL;Dong ZB;Wei YH;Yang CL .Marangoni convection and weld Shape variation in A-TIG welding process[J].Theoretical and Applied Fracture Mechanics,2007(2):178-186. |
| [6] | Howse D.;Lucas W. .Activating flux-increasing the performance and productivity of the TIG and plasma processes[J].Welding & Metal Fabrication: Welding and Joining Practice and Technology,1996(1):11-17. |
| [7] | 杨春利,牛尾诚夫,田中学.TIG电弧活性化焊接现象和机理研究（2）--活性化TIG焊接中的电弧现象[J].焊接,2000(05):15-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%