邻菲罗啉(PHEN)及其衍生物可有效抑制金属及其合金在酸性介质中的腐蚀,但目前还未见其对铜材缓蚀的报道.采用失重法及扫描电镜(SEM)研究了PHEN及其衍生物2-苯基-1H-咪唑[4,5-f][1,10]邻菲罗啉(PIPH)这2种有机缓蚀剂在1 mol/L HCl溶液中对铜的缓蚀作用,并对其缓蚀机理进行探讨.结果表明:当缓蚀剂浓度为1.0 mmol/L、温度为30℃,吸附成膜时间4h,2种缓蚀剂在1 mol/L HCl溶液中的缓蚀效率均达最大值,PHEN和PIPH对铜的缓蚀效率可分别达到96.4％和99.7％;2种缓蚀剂在铜表面的吸附均符合Langmuir吸附模型,且均为化学吸附.
参考文献
| [1] | 郭强,逯凯丽,王洋霞,赵红艳,张石文,王林.邻菲罗啉与溴离子对磷酸溶液中冷轧钢的缓蚀研究[J].云南化工,2013(03):1-6,16. |
| [2] | Li X H;Deng S D;Xie X G .Experimental and theoretical study on corrosion inhibition of o-phenanthroline for aluminum in HCl solution[J].Journal of the Taiwan Institute of Chemical Engineers,2014,45(4):1865-1875. |
| [3] | Obi-Egbedi N O;Obot I B;Eseola A O .Synthesis,characterization and corrosion inhibition efficiency of 2-(6-methylpyridin-2-yl)-1 H-imidazo[4,5-f][1,10]phenanthroline on mild steel in sulphuric acid[J].Arabian Journal of Chemistry,2014,7(2):197-207. |
| [4] | Fan S H;Zhang A G;Ju C C et al.A Triphenylamine-Grafted Imidazo[4,5-f][1,10]phenanthroline Ruthenium(Ⅱ)Complex:Acid Base and Photoelectric Properties[J].Inorganic Chemistry,2010,49(8):3752-3763. |
| [5] | 张光华,王腾飞,孙卫玲,董惟昕,费菲.硫脲基烷基咪唑啉类缓蚀剂的制备、缓蚀性能及其机理[J].材料保护,2011(02):21-23,58. |
| [6] | 王克诚,刘欣,王丽红,刘妍.聚天冬氨酸及其与葡萄糖酸钠复配物对碳钢的缓蚀性能研究[J].材料保护,2007(06):60-62. |
| [7] | Bobina M;Kellenberger A .Corrosion resistance of carbon steel in weak acid solutions in the presence of L-histidine as corrosion inhibitor[J].Corrosion Science,2013,69:389-395. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%