探讨了高温下喷丸强化(SP)因素(残余压应力引入、表面粗糙度增大、表面加工硬化等)对Ti811钛合金微动疲劳(FF)抗力的作用规律和机制.结果表明,SP处理可以有效地提高350℃高温下Ti811合金的微动疲劳抗力,但对500℃下FF抗力有不利影响;SP引入的表层残余压应力增加裂纹闭合力,是SP提高350℃高温下钛合金FF抗力最为重要的因素,SP表面加工硬化的作用为次要因素;SP造成的粗糙度增大在350℃和500℃高温下对钛合金的FF抗力呈现出不利的作用,原因是表面机械损伤的影响突出,这种影响与残余压应力的存在状态有关.
参考文献
| [1] | Wu Ling-ling;Holloway B C .[J].Surface and Coatings Technology,2000,130(02):207. |
| [2] | Xue L;Koul A K;Bibby M.[A].Milan:Computational Mechanics Pub,1995:265. |
| [3] | Dyer J P;Conway J C;Hoeppner D W;Chandrasekaran V.[A].West Conshohocken:ASTM Press,2000:491. |
| [4] | Hoeppner D;Adibnazari S .Literature Review and Preliminary Studies of Fretting and Fretting Fatigue Including Special Application to Aircraft Joints[R].Salt Lake:Department of Mechanical Engineering,University of Utah,1994. |
| [5] | Waterhouse R B;Trowsdale A J .[J].Journal of Physics D:Applied Physics,1992,25A:236. |
| [6] | Labedz J;Waterhouse R B;Niku-Lari A.Metal Treatments Against wear,Corrosion,Fretting,and Fatigue[M].Oxford:Pergamon Press,1988:87. |
| [7] | 刘道新,何家文.喷丸强化因素对Ti合金微动疲劳抗力的作用[J].金属学报,2001(02):156-160. |
| [8] | 赵永庆,朱康英,李左臣.Ti811合金的热稳定性能[J].稀有金属材料与工程,1997(03):35-39. |
| [9] | 赵永庆,刘炳南.合金成份对Ti811合金棒材性能的影响[J].稀有金属材料与工程,1994(03):59-64. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%