目前,就热浸镀锌助镀剂中Ni盐含量的变化对镀层的影响研究报道不多.将低碳钢退火板采用不同NiCl2含量的助镀剂助镀后热浸镀锌,并采用扫描电子显微镜(SEM)、光学显微镜(OM)对镀层的厚度、结构、形貌及成分进行分析.结果表明:NiCl2含量在0～6 g/L内,锌镀层质量及厚度随着氯化镍含量的增加而减小,NiCl2含量超过6 g/L时,则不随氯化镍的增加而变化;氯化镍会增加锌镀层中δ金属间化合物相的厚度,细化ζ金属间化合物相,使ζ金属间化合物相更加致密,并减少ζ金属间化合物相的厚度,对η金属间化合物相影响无影响.
参考文献
| [1] | Verma A R B;Van Ooij W J .High-temperature batch hotdip galvanizing.Part 1.General description of coatings formed at 560 ℃[J].Surface and Coatings Technology,1997,89(01):132-142. |
| [2] | Pistofidis N;Vourlias G;Konidaris S;Pavlidou E;Stergioudis G;Tsipass D .The effect of preflux bath additives on the morphology and structure of the hot-dip galvanized coatings[J].Crystal Research and Technology: Journal of Experimental and Industrial Crystallography,2006(8):759-765. |
| [3] | Yuttanant Boonyongmaneerat,Kanokwan Saengkiettiyut,Pranee Rattanawaleedirojn,Charttanong Angkaprasert,Jumpot Wanichsampan,Sawalee Saenapitak.Effect of NiCl2-Based Fluxes on Interfacial Layer Formation of Hot Dip Galvanized Steels[J].钢铁研究学报（英文版）,2010(08):74-78. |
| [4] | 李俊红.锌镍合金的研制[J].有色金属（冶炼部分）,2006(03):51-53. |
| [5] | 张启富;刘邦津;黄建中.现代钢带连续热镀锌[M].北京:冶金工业出版社,2007:114-115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%