在1103K,3min～30min条件下,使用72Ag-28Cu共晶钎料对TC4/TC4进行了钎焊试验.研究表明随钎焊时间增加,钎料中铜原子大量向界面迁移富集,母材Ti原子不断向钎缝溶解,在随后的冷却过程中产生共析转变并形成α-Ti+Ti2Cu.试样加载1MPa,钎焊时间3min时接头常温拉伸强度为221MPa,延长钎焊时间接头强度呈增加趋势,30min时母材与钎缝界面模糊,此时强度最高达到373MPa,与不加载相比,强度平均增幅达80MPa左右.
参考文献
| [1] | Tadao Onzawa;Akio Suzumura;Myoungwan Ko .Structure and Mechanical Properties of TiG and Ti- 6Al- 4V Alloy Brazed Joints with Ti- based Amorphous Filler Metals[J].Quarterly Journal of Japan Welding Society,1987,5(02):205. |
| [2] | Ken Sasabe;Kazuo Hirano .Brazing of Titanium with Ti- Cu- Cr Filler Alloy[J].Quarterly Journal of Japan Welding Society,1990,8(03):354. |
| [3] | Elrood D .Contractor Rep[R].No. NASA- CR- 3418, NASA,1981. |
| [4] | Kaarlela W T;Margolis W S .[J].Welding Journal,1974,53(10):629. |
| [5] | Adao Onzawa;Akio Suzumura;Myoungwan Ko .Microstructure of Titanium Joint Made with Ti- Zr Base Brazing Fillers[J].Quarterly Journal of Japan Welding Society,1989,7(02):455. |
| [6] | 虞觉常.Binary Alloy Phases Diagrams[M].上海:上海科学技术出版社,1984:350. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%