本文首先在最佳掺杂的La1.85Sr0.15CuO4体系中用6％的Ti4+取代Cu2+使其超导电性完全消失,然后用空穴注入法掺杂成功地合成了La2-xSrCu0.94Tio.06O4(0.15≤x≤0.39)系列多晶样品,并用X光衍射、红外透射光谱和拉曼光谱等实验手段对样品的结构、微结构以及样品中CuO6八面体的振动模进行了系统地研究.红外透射光谱和拉曼光谱测量研究结果表明,被注入的空穴将补偿那些围绕在杂质Ti周围的电子,这将导致Ti的有效价态降低并弱化CuO2面上的不对称性,使那些近邻杂质的被局域化的空穴重新变成巡游载流子,进而将重新开始对超导电性负责.
参考文献
| [1] | Lynch, M.S.;Slenkamp, K.M.;Cheng, M.;Khalil, M. .Coherent fifth-order visible-infrared spectroscopies: Ultrafast nonequilibrium vibrational dynamics in solution[J].The journal of physical chemistry, A. Molecules, spectroscopy, kinetics, environment, & general theory,2012(26):7023-7032. |
| [2] | Lampakis D.;Liarokapis E.;Panagopoulos C.;Cooper JR. Ehrenberg H.;Hartmann T.;Palles D. .Phase transitions and Raman spectra correlations in La2-xSrxCuO4(0.0 <= x <= 0.45)[J].Physical Review.B.Condensed Matter,2000(13):8811-8817. |
| [3] | McQueeney RJ.;Egami T.;Yethiraj M.;Shirane G.;Endoh Y.;Petrov Y. .Anomalous dispersion of LO phonons in La1.85Sr0.15CuO4 at low temperatures[J].Physical review letters,1999(3):628-631. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%