本文采用扫描Kelvin探针、扫描振动电极等方法表征了NaCl液滴覆盖下Q235钢表面的微区电化学参数分布的特征.结果证实,NaCl液滴下碳钢表面的电位分布和电流密度分布是不均匀的,中心为阳极区,边缘为阴极区.液滴中心和边缘阴阳极电位相差0.4 V,阴阳极电流密度相差o.9 μA/cm2.NaCl液滴下碳钢表面电化学参数的不均匀分布导致液滴边缘发生强烈的阴极极化,导致附近区域碱性化是微液滴形成的主要原因.
参考文献
| [1] | 王振尧,于国才,韩薇.我国自然环境大气腐蚀性调查[J].腐蚀与防护,2003,24(8):323. |
| [2] | 张先勇,舒德学,陈建琼.海南万宁试验站大气环境及腐蚀特征研究[J].装备环境工程,2005,2(4):73. |
| [3] | Wang J,Tsuru T.Potential distribution and micro-droplets formation on the metal with salt particle deposition[A].The 204th Meeting of the Electrochemical Society,Orlando:The Electrochemical Society,Inc.,2003,D2:472. |
| [4] | Tsuru T,Tamiya K I,Nishikata A.Formation and growth of micro-droplets during the initial stage of atmospheric corrosion[J].Electrochim.Acta,2004,(49):2709. |
| [5] | Zhang J B,Wang J,Wang Y H.Electrochemical investigations of micro-droplets formed on metals during the deliquescence of salt particles in atmosphere[J].Electrochem.Commun.,2005,(7):443. |
| [6] | Zhang J B,Wang J,Wang Y H.Phenomenon of micro-droplets formation on metals during the deliquescence of salt particles in atmosphere[J].物理化学学报,2005,21(9):993. |
| [7] | 张际标,王佳,王燕华.大气腐蚀起始过程中的微液滴现象研究[J].装备环境工程,2005,2(5):14. |
| [8] | 张际标.中国科学院研究生院博士学位论文[D].青岛,2005. |
| [9] | 张际标,王燕华,姜应律等.微液滴现象与大气腐蚀-Ⅰ微液滴的形成与扩展[J].中国腐蚀与防护学报,2006,26(4):207. |
| [10] | 梁利花,姜应律,王佳.溶液性质对微液滴形成的影响[J].高等学校化学学报,2006,(11):27. |
| [11] | Wang J,Liang L H,Jiang J.The role of electrochemical polarization in micro-droplets formation[J].Electrochem.Commun.,2008,10:1788. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%