采用低压金属有机化学气相外延(LP-MOCVD)法生长Mg掺杂p型GaN薄膜,利用高分辨X射线衍射(HRXRD)技术研究不同退火时间对GaN薄膜中外延应变的影响.研究发现应变状态随退火时间变化而发生改变.退火前水平方向为压应变.在小于最佳退火时间(15min)的时间范围内进行退火时,由于受杂质Mg在退火过程中热扩散、替位行为引起的晶格畸变以及受主中心与价带之间的电子跃迁引起的电子效应等多种因素的影响,水平应变状态由压应变向张应变转变且随时间增加应变逐渐增强.退火时间增至30min时,由于N空位增多和复合体MgGs-VN的形成以及热应力等因素的多重影响,应变状态转变为压应变.
参考文献
| [1] | Wu Y F;Keller B P;Keller S et al.[J].Solid-State Electronics,1997,41(10):1569-1574. |
| [2] | Shuji Nakamura;Masayuki Senoh;Shin-ichi Nagahama .Blue InGaN-based laser diodes with an emission wavelength of 450 nm[J].Applied physics letters,2000(1):22-24. |
| [3] | Nskarmura S;Pearton S;Fasol G.The Blue Laser Diode:The Complete Story[M].Beilin:Springer-Verlag,2000:152. |
| [4] | 施锦行 .[J].半导体情报,1998,35(01):42-45. |
| [5] | 徐波,余庆选,吴气虹,廖源,王冠中,方容川.应力和掺杂对Mg：GaN薄膜光致发光光谱影响的研究[J].物理学报,2004(01):204-209. |
| [6] | Williamson G K;Hall W H .[J].Acta Metallurgy,1953,1(01):22-31. |
| [7] | Tomita K;Itoh K;Ishiguro O et al.[J].Journal of Applied Physics,2008,104(01):1906-1910. |
| [8] | Pozina G;Hemmingsson C;Paskov P P et al.[J].Applied Physics Letters,2008,92(15):1904-1906. |
| [9] | Hwang JD;Yang GH .Activation of Mg-doped P-GaN by using two-step annealing[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(10):4694-4697. |
| [10] | Akasaki I;Amano H;Kito M et al.[J].Journal of Luminescence,1991,48(49):666-670. |
| [11] | 丁志博,姚淑德,王坤,程凯.Si（111）衬底上生长有多缓冲层的六方GaN晶格常数计算和应变分析[J].物理学报,2006(06):2977-2981. |
| [12] | Powell R G;Lee N E;Kim Y W et al.[J].Journal of Applied Physics,1993,73(04):189-195. |
| [13] | Stress and its effect on optical properties of GaN epilayers grown on Si(111), 6H-SiC(0001), and c-plane sapphire[J].Applied physics letters,2003(4):677-679. |
| [14] | 吴学华;吴自勤 .[J].物理学报,1999,28(01):44-47. |
| [15] | 邢艳辉,韩军,邓军,刘建平,牛南辉,李彤,沈光地.p型氮化镓不同掺杂方法研究[J].功能材料,2007(07):1123-1124,1131. |
| [16] | Chris G;Van de Walle .[J].Physical Review B:Condensed Matter,2003,68(16):1829-1832. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%