对某500 kV输电线路铁塔塔脚出现严重腐蚀的现场宏观检查,对上底座腐蚀产物取样进行XRD,SEM和EDS分析.结果表明,塔脚的腐蚀是发生在上底座和护板表面的局部腐蚀,主要是大气中SO2对塔脚造成的腐蚀.塔脚所处的位置SO2浓度最高,而锌和A3钢在SO2存在的条件下,腐蚀速率都高于在纯空气中(不含SO2),生成的腐蚀产物结构多孔疏松,且铁塔经常处于潮湿条件下的服役环境能够满足腐蚀持续进行的电化学条件.这些因素共同作用,导致塔脚的腐蚀速率很高,在1～2 a的时间内腐蚀减薄已达50％.根据对腐蚀原因的分析,制定了相应的焊补加固和防腐蚀涂料体系方案.
参考文献
| [1] | 何长华.输电线路铁塔用钢的发展趋势[J].电力建设,2010(01):45-48. |
| [2] | 陈云,强春媚,王国刚,苗文华.输电铁塔的腐蚀与防护[J].电力建设,2010(08):55-58. |
| [3] | Pareja RR;Ibanez RL;Martin F;Ramos-Barrado JR;Leinen D .Corrosion behaviour of zirconia barrier coatings on galvanized steel[J].Surface & Coatings Technology,2006(22/23):6606-6610. |
| [4] | Shibli SMA;Jayalekshmi AC;Remya R .Electrochemical and structural characterization of the mixed oxides-reinforced hot-dip zinc coating[J].Surface & Coatings Technology,2007(16/17):7560-7565. |
| [5] | Bastos AC;Ferreira MGS;Simoes AM .Comparative electrochemical studies of zinc chromate and zinc phosphate as corrosion inhibitors for zinc[J].Progress in Organic Coatings: An International Review Journal,2005(4):339-350. |
| [6] | C. ARROYAVE;F.A. LOPEZ;M. MORCILLO .THE EARLY ATMOSPHERIC CORROSION STAGES OF CARBON STEEL IN ACIDIC FOGS[J].Corrosion Science,1995(11):1751-1761. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%