CO2共聚物为基聚氨酯泡沫体与弹性体降解性能的比较研究

高分子材料科学与工程, 2001, 17(1): 173-175.

CO2共聚物为基聚氨酯泡沫体与弹性体降解性能的比较研究

邹新伟 ^1, , 杨淑英 ^2, , 陈立班 ^3, , 江英彦 ^4,

1.机械部广州电器科学研究所

2.中国科学院广州化学研究所

3.中国科学院广州化学研究所

4.中国科学院化学研究所

基金项目: 国家自然科学基金

关键词：二氧化碳共聚物 , 聚氨酯泡沫体 , 生物降解性

STUDY ON COMPARISON OF DEGRADABILITIES OF POLYURETHANES FOAMS AND ELASTOMERS BASED ON CO2 COPOLYMERS

讨论以高分子负载的双金属(PBM)催化剂合成的CO2共聚物——聚碳酸亚乙酯(PEC)为基的聚氨酯泡沫体在活性污泥和70 ℃加热水解条件下的降解性能,并与聚碳酸亚乙酯-聚氨酯弹性体的降解性进行了比较。结果表明,这种泡沫体材料的降解速度远大于其弹性体的降解速度。

The degradabilities of polyurethanes(PU) foams based on copolymer from CO2 catalyzed with polymer chelated bimetal catalyst(PBM)-poly(ethylene carbonate)(PEC) under the conditions of activated sludge and thermal hydrolysis(70 ℃) were discussed. The degradabilities of PEC-PU elastomers and foams were compared. The test results show that the rate of degradation of PEC-PU foams are much faster than that of PEC-PU elastomers. The percent of weight-loss PEC-PU foams is 31% after 40 days in activated sludge. The foams of PEC-PU may be used in degradable packing materials.

参考文献

[1]	杨惠娣 .[J].中国塑料,1997,10(04):1-9.
[2]	邹新伟;杨淑英;陈立班.[J].化学世界,1997(09):1-3.
[3]	Chen Liban;Makromol .[J].Chemical Macromol Symp,1992,59:75-82.
[4]	邹新伟,杨淑英,陈立班,江英彦.二氧化碳共聚物为基聚氨酯的生物降解性研究[J].化学通报,1998(10):55-57.
[5]	Masar B;Cefelin P.[J].Journal of Applied Polymer Science,Applied Polymer Symposium,1979:259-268.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网