采用溶胶-凝胶法制备了Ag掺杂纳米二氧化钛.采用SEM、XPS、XRD、UV-Vis对样品进行表征.结果表明,未掺杂的样品的粒径在80～100nm,Ag掺杂的样品的粒径在40～50nm;Ag元素成功进入晶格,含量为0.67%(原子分数);400℃热处理时,掺杂与未掺杂样品晶型基本相同,600℃热处理时,掺杂能够抑制样品晶型的转变;掺杂使二氧化钛的吸收带边发生了一定的红移.在此条件下Ag的最佳掺杂量为0.5%,最佳热处理温度为600℃.在最佳条件下,以甲基橙为模拟污染物,经过120min的光催化实验,降解率达到97.9%.
参考文献
| [1] | Shu Y;Masakazu K;Zhang Q W et al.[J].Materials Science,2007,42:2399-2404. |
| [2] | Venkatachalam N;Palanichamy M;Murugesan V et al.[J].Catalysis Communications,2007,8:1088-1093. |
| [3] | Asahi R;Morikawa T;Ohwaki T et al.[J].Science,2001,293(13):269-271. |
| [4] | Sakthivel S;Kisch H .[J].Angewandte Chemie International Edition,2003,42(40):4908-4911. |
| [5] | Wang JS.;Yin S.;Zhang QW.;Saito F.;Sato T. .Mechanochemical synthesis of SrTiO3-xFx with high visible light photocatalytic activities for nitrogen monoxide destruction[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2003(9):2348-2352. |
| [6] | Ohnao T;Akiyaoshi M;Umebayashi T et al.[J].Appli Cataly A General,2004,265(01):115-121. |
| [7] | Masashi I;Li J G;Takamasa I et al.[J].Thin Solid Films,2007,1:5. |
| [8] | 薛寒松,李华基,易于,胡慧芳,孟翠.铈掺杂二氧化钛纳米管的光催化性能[J].机械工程材料,2008(06):36-39,65. |
| [9] | 梁春华,吴峰.钐离子掺杂二氧化钛光催化降解甲基橙研究[J].环境保护科学,2008(02):45-47. |
| [10] | 李振华,刘中清,燕青芝,王宜超,葛昌纯.合成温度对二氧化钛纳米管的影响[J].功能材料,2007(03):485-487,491. |
| [11] | Khan S U M;Al-Shahry M;Ingler W B .[J].Science,2002,297:2243. |
| [12] | Choi Y;Umebayashi T;Yamamoto S et al.[J].Journal of Materials Science Letters,2003,22:1209. |
| [13] | Chourasia A R;Chopra D R;Mcguire G E et al.[J].Surface Science Spectra,1992,1:233-237. |
| [14] | Chourasia A R;Chopra D R .[J].Thin Solid Films,1995,266:298. |
| [15] | Shankar K;Tep K C;Mor G K et al.[J].Journal of Physics D:Applied Physics,2006,39:3150. |
| [16] | 余志勇,张维,马明,崔晓莉.阳极氧化TiN薄膜制备N掺杂纳米TiO2薄膜及其可见光活性[J].物理化学学报,2009(01):35-40. |
| [17] | Masashi I;Li J G;Takamasa I et al.[J].Thin Solid Films,2007,1:5. |
| [18] | 唐丽娜,柳丽芬,董晓艳,杨凤林.金属掺杂二氧化钛光催化还原硝酸氮[J].环境科学,2008(09):2536-2541. |
| [19] | 王卫伟,张志焜.铁离子对二氧化钛晶型转变的影响[J].功能材料,2003(04):429-430. |
| [20] | Choi W;Termin A;Michael R H .[J].Journal of Physical Chemistry,1994,98(51):13669-13679. |
| [21] | 张立德;牟季美.纳米材料和纳米技术[M].北京:科学出版社,2001 |
| [22] | 张志琨;崔作林.纳米技术与纳米材料[M].北京:国防工业出版社,2000 |
| [23] | Zhao L;Jiang Q;Lian J S .[J].Application Surface Sinence,2008,254:4620. |
| [24] | 宁成云,王玉强,郑华德,谭帼馨,陈晓峰,马强,刘绪建.Cu掺杂二氧化钛纳米管阵列的研究[J].硅酸盐通报,2009(04):775-778. |
| [25] | 刘秀华 .金属离子掺杂二氧化钛光催化剂的改性研究[D].绵阳:中国工程物理研究院,2007. |
| [26] | 崔玉民,范少华,张颖.稀土掺杂TiO2纳米微粒的合成、表征及光催化活性[J].北京科技大学学报,2006(10):956-958. |
| [27] | 刘秀珍,施利毅,华彬.二氧化钛形态结构及其光催化活性的研究进展[J].上海环境科学,2000(09):414-417. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%