Bright long afterglow phosphorescence glasses were prepared by using SrAl2O4 : Eu2+, Dy3+ phosphors and suitable glass frits together. The SrAl2O4 : Eu2+, Dy3+ phosphors were initially prepared by the solid reaction method. Three kinds of glass frits were prepared to match the SrAl2O4 : Eu2+, Dy3+ phosphors. Effects of the compositions of the glass frits, the ratios of the phosphors to the frits as well as the firing temperature and firing times on the properties of the samples were discussed. XRD analysis indicated the samples exhibited the typical diffraction peaks of SrAl2O4 : Eu2+, Dy3+. The emission spectra of the samples showed broad bands peaking at 510nm.The excitation spectra of the samples showed broad bands ranging from 300 to 480nm. These are believed due to the 5d4f-4f transitions of Eu2+ in the SrAl2O4 : Eu2+, Dy3+ phosphors. The afterglow luminescence of the samples excited by a 40W fluorescence lamp for 30min can be observed in the dark for more 10h with the naked eyes. It can find wide applications in many fields.
关键词:
long afterglow
,
null
,
null
,
null
张玉柱
,
雷云波
,
李俊国
,
邢宏伟
,
韩志杰
,
龙跃
钢铁钒钛
采用扫描电子显微镜和化学分析方法对三种不同方式处理的钢渣中f-CaO的显微形貌及含量进行分析研究,试验结果表明,钢渣中弥散型f-CaO主要形成于C2S和C3S初晶、RO相形成和C3S分解等过程,其数量多、分布广、粒径较小；缓冷渣中氧化钙的典型显微形貌为灰色圆粒状、薄膜状、细小长条状；气淬渣中氧化钙的典型显微形貌为灰色薄膜状和细小长条状；热焖渣中氧化钙典型显微形貌为细小长条状；冷却强度对钢渣中f-CaO含量影响显著,因此冷却强度最弱的缓冷渣中f-CaO含量达到了6.96％,而冷却强度最高、经过水解的热焖渣中f-CaO含量只有0.55％；前期冷却强度高、后期冷却强度弱的气淬渣中f-CaO含量为2.28％；降低气淬钢渣粒径,可降低渣中f-CaO含量,从而提高其综合利用价值.
关键词:
钢渣
,
冷却强度
,
自由氧化钙
,
显微形貌
,
缓冷渣
,
气淬渣
,
热焖渣
李辉
,
史诗
,
冯绍航
,
沈宝镜
,
张巨清
硅酸盐通报
本文采取加消解剂、磨细、加分散剂三种方式组合对用循环流化床锅炉低温烧成的高钙粉煤灰进行处理,以消解其中的f-CaO.分析按不同方式处理后高钙粉煤灰中f-CaO的含量,并利用扫描电镜观察f-CaO消解后的形貌变化.试验结果表明:未添加分散剂条件下,消解剂量对f-CaO消解的影响最大,其次为粉磨时间,最后为消解时间;添加分散剂有助于水分由粉煤灰颗粒表面孔隙进入其内部,加快f-CaO消解.扫描电镜观察显示仅加消解剂处理高钙粉煤灰中的f-CaO消解后生成了呈六方片状、板状和短柱状的Ca(OH)_2;而加消解剂同时加入分散剂,不光在高钙粉煤灰颗粒表面,在其内部也生成大量簇状的Ca(OH)_2.
关键词:
高钙粉煤灰
,
f-CaO消解
,
消解剂
,
粉磨
,
分散剂
陈华
,
李辉
,
顾恒星
,
杨刚
,
陈伟
,
徐德龙
硅酸盐通报
采用水泡陈化方法处理滚筒钢渣,跟踪检测滚筒钢渣中游离氧化钙(f-CaO)含量.运用高斯过程回归,建立基于高斯过程回归的软测量模型预测滚筒钢渣水泡陈化中f-CaO含量.结果表明,水泡陈化方法处理滚筒钢渣可以有效降低f-CaO含量,A类滚筒钢渣120 d之后f-CaO含量基本维持在3.98%~4.03%,B类滚筒钢渣105 d之后f-CaO含量维持在9.84%~10.03%,满足安全利用的要求;基于高斯过程回归的软测量模型的真实值与预测值数据吻合较好,相对误差为-1.493%~0.748%,有效提高了滚筒钢渣水泡陈化中f-CaO含量预测精度.
关键词:
水泡陈化
,
滚筒钢渣
,
高斯过程回归
,
游离氧化钙
,
软测量
周曦亚
,
胡俊
,
周斌扬
,
刘林凤
硅酸盐通报
采用烧结法制备了CaO-SiO_2-R_2O-F(R=Na, K)系微晶玻璃,并结合XRD、DTA、SEM等测试方法,探讨了CaF_2含量对CaO-SiO_2-R_2O-F系微晶玻璃晶化行为的影响.结果表明:添加适量的CaF_2能有效地促进微晶玻璃的析晶.在一定热处理制度下,制备出的微晶玻璃内含大量互锁的板条状晶体和针状晶体,主晶相为硅碱钙石和Frankamenite(一种富含氟的硅碱钙石).随着CaF_2含量的增加,晶体的含量逐渐提高,晶体数量逐渐增大,尺寸逐渐减小.
关键词:
微晶玻璃
,
硅碱钙石
,
晶化行为
,
显微结构
田清波
,
王修慧
,
徐丽娜
,
林晓娟
,
高宏
稀有金属材料与工程
为了研究P2O5及氟化物对CaO-MgO-Al2O3-SiO2系微晶玻璃形成及析晶的影响,采用高温熔融法制备了不同P2O5及氟化物含量的玻璃试样.结果表明:玻璃的形成范围大致为(P2O5%+F%)≤10%.在氟化物的添加量较低时,试样仅发生表面析晶,析出晶体为硅灰石(CaSiO3)和少量的钙长石(CaAl2Si2O8).随着氟化物含量是增加,试样在表面和内部都析出晶体,最终形成"整体"析晶的状态.P2O5的加入抑制了表面析晶,但促进了玻璃的分相和整体析晶.同时添加P2O5及氟化物将促进晶体的整体析出和晶体的生长,P2O5加入量的提高有利于氟磷灰石[Ca5(PO4)3F]的析出,而氟化物含量的提高增加了钙长石的析出.
关键词:
微晶玻璃
,
析晶
,
组织结构
,
CaO-MgO-Al2O3-SiO2玻璃
田清波
,
徐丽娜
,
石磊
,
尹衍升
硅酸盐通报
doi:10.3969/j.issn.1001-1625.2007.02.038
应用扫描电子显微镜、X射线衍射及示差扫描量热法等技术研究了一种SiO2-Al2O3-CaO-MgO-Fe2O3-ZrO-F玻璃陶瓷析晶特征和组织形貌.结果表明:玻璃转变温度为725 ℃左右,在730 ℃后形成了分布均匀的孔状非晶态分相现象.在第一放热峰温度(820 ℃)析晶时,玻璃样品为表面析晶,析出晶体为钙长石(CaAl2Si2O8)和硅灰石(CaSiO3).从表面向内部分别形成枝状晶体、枝状晶体和粒状晶体、粒状晶体三层不同的表面析晶形态.在1040 ℃保温后,玻璃样品中表面析晶和整体析晶共存,析出晶相均以钙长石为主.
关键词:
玻璃陶瓷
,
复合添加剂
,
析晶
,
组织形态