佟媛媛
,
华勤
上海金属
doi:10.3969/j.issn.1001-7208.2010.03.011
运用热分析技术研究了冷却曲线特征值与319铝合金中化学成分之间的关系,并进行回归分析.结果表明,在不考虑工艺因素的情况下,试样的硅含量与α-Al枝晶生长回升温度TαDENG之间的相关性最大,相关系数r为-0.65,以硅含量可预测α-Al枝晶生长回升温度.在浇注过程中,冷却速度与α-Al枝晶生长回升温度TαDENG密切相关,相关系数为r=-0.72.在相同的冷却条件下,铝合金的浇注温度和浇注量对冷却速度有明显的影响,因此,可以通过调整浇注温度和浇注量,控制铝合金的冷却速度,进而也可预测铝合金中α-Al枝晶生长回升温度TαDENG.
关键词:
319铝合金
,
热分析
,
特征值
,
浇注工艺
Transactions of Nonferrous Metals Society of China
A new process for the hydrometallurgy of refractory gold concentrates was presented. The process comprises grinding-leaching, intensified alkaline leaching (IAL), cyanidation and adsorption. In a stirring-type pulverizing-leaching tower mill, the concentrate is ground to <35. 6 μm of 95. 5 % while simultaneously leached by NaOH of 12 kg/t, then carried out intensified alkaline leaching for 48 h by NaOH of 108 kg/t in enhanced agitation tanks with the pulp concentration of 40% solids at the environmental temperature of 9. 5 &SIM; 13. 5 &DEG;C and the environmental pressure of 10(5) Pa. The oxidation rate of As is 94. 9%, and 47. 6% for S. The total consumption of NaOH is only 20% of that theoretically calculated under the conditions of full oxidation at the same oxidation rates of arsenic to arsenate and sulfur to sulfate. The gold leaching rate by NaCN in 24 h is increased from 9. 2% before pretreatment to 94. 2%. The consumption of NaCN is 7. 5 kg/t, which is one times less than that before pretreatment. The extraction cost of gold is about 422 Yuan/t.
关键词:
refractory gold concentrates;grinding-leaching;intensified alkaline;leaching (IAL);pretreatment;common temperature and pressure
Journal of Applied Physics
Motivated by the recent experimental fabrication of half-metallic MnSb and CrSb thin films with metastable zinc-blende structure [Aldous et al. Phys. Rev. B 85, 060403(R) (2012); Deng et al. J. Appl. Phys. 99, 093902 (2006)], we investigate the structural, electronic, and magnetic properties of TiSb in both ground-state NiAs and metastable zinc-blende phases by using the first-principles calculations. It is shown that the ground-state NiAs phase is metallic and nonmagnetic, but the metastable zinc-blende phase exhibits half-metallic ferromagnetism with a magnetic moment of 1.00 mu(B) per formula unit. We also reveal that the half-metallicity in bulk ZB TiSb is lost at the Sb-terminated (001) surface due to the appearance of surface states within the gap of the minority-spin channel, but the Ti-terminated (001) surface retains the bulk half-metallicity, which makes ZB TiSb a promising candidate for the possible epitaxial growth of half-metallic thin films or multilayers on semiconductor substrates for spintronic applications. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4739744]
关键词:
room-temperature ferromagnetism;molecular-beam epitaxy;crsb;cras;spintronics;state;mnas