WU Shengli
,
WANG Qingfeng
,
BIAN Miaolian
,
ZHU Juan
,
LONG Fangyi
钢铁研究学报(英文版)
The influence of iron ore characteristics on FeO formation during sintering was examined mainly in terms of chemical composition and the melting characteristics of iron ores. Statistical regression and Xray diffraction were used to further explain the specific effect of iron ore characteristics on FeO formation. The results indicate that LOI (loss on ignition) in iron ores have a positive influence on FeO formation by promoting the sintering process of Fe2O3 decomposing and reducing. Silica contents in iron ores play a determining role in final content of FeO in sinter. The melting characteristics of iron ores significantly affect FeO formation during sintering.
关键词:
iron ore characteristic
,
chemical composition
,
melting characteristic
,
FeO formation
吴向东
,
万敏
,
周贤宾
材料科学与工艺
doi:10.3969/j.issn.1005-0299.2004.04.015
针对建立的十字形双向拉伸试验系统,利用有限元模拟优化得到的十字形试件,采用载荷控制方式对SPEN钢板和2024-O铝合金板进行了不同加载路径下的双向拉伸试验,得到了不同硬化阶段下的实验屈服轨迹,并与现有屈服准则Hill48、Hill79、Hill90、Hill93、Gotoh、Hosford、Barlat-Lian以及Mises的理论屈服轨迹进行了对比.结果表明:对于SPEN钢板,Hosford各向异性屈服准则得到的理论屈服轨迹与实验屈服轨迹符合得最好,其次是Mises屈服准则,Hill48屈服准则最差;对2024-O铝合金板,Barlat89、Hosford屈服轨迹与实验屈服轨迹符合得最好,Mises屈服准则最差.
关键词:
双向拉伸试验
,
十字形试件
,
各向异性
,
屈服准则
邹俭鹏
,
阮建明
,
黄伯云
,
周忠诚
材料研究学报
doi:10.3321/j.issn:1005-3093.2005.03.007
制备了HA(ZrO2)/316L不锈钢纤维对称功能梯度材料(FGM),316L不锈钢纤维的含量(体积分数)按20%→10%→0→10%→20%呈轴向对称梯度变化.分析了材料的微观结构和微区元素含量,研究了材料的性能与316L不锈钢纤维含量的关系.结果表明,在HA(ZrO2)/316L不锈钢纤维对称FGM中,316L不锈钢纤维在微观上呈无序和均匀分布状态,它被包裹于HA(ZrO2)基体中,两者紧密结合.316L不锈钢纤维与HA(ZrO2)基体间的界面表现为部分凹凸不平,紧紧地咬合在一起.在FGM基体中发生了微量的韧化相Fe元素扩散,在韧化相316L不锈钢纤维不发生基体相Ca、P元素的扩散,基体与韧化相之间不发生化学反应.随着316L不锈钢纤维含量的增加,HA(ZrO2)/316L不锈钢纤维复合材料的断裂韧性和弹性模量逐渐增加,体现了FGM中各梯度层的力学性能缓和设计.按Miao模型计算HA(ZrO2)/316L不锈钢纤维FGM中的残余热应力为515 MPa,FGM的增韧机理主要为纤维的拔出增韧和层间的裂纹偏转增韧.
关键词:
复合材料
,
功能梯度材料
,
生物材料
,
羟基磷灰石
,
316L不锈钢纤维
,
热等静压