HAN Qingyou HU Hanqi Beijing University of Science and Technology
,
Beijing
,
China [Originally published in ACTA METALL SIN (CHINESE EDN) 24 (5) 1988 pp B320—B324
,
received 29 August 1986
,
in revised form 5 March 1987]
金属学报(英文版)
The gradient of the equilibrium melting temperature distribution at the advancing liquid-solid interface of liquid side was derived.From which,a parameter,H,used for evaluating the abili- ty of grain refinement of solute elements was proposed.Experiments on Al-based alloys show that the grain size decreases as the value of parameter,H,increases.Such a dependance indi- cates that the parameter H can be used for choosing grain refiner.
关键词:
solute elements
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,