金属学报(英文版)
Theconstruction changinginthereversetransformation ofthestress induced εMin Fe 17 Mn 10 Cr 5 Si 4 Ni alloy is carefully inspected in transmission electron microscope, and then stress induced εM procedure of reverse transformation is analyzed. The behavior of reverse transformationisdissimilar when the organization of εMis different. The reversetransfor mation ofεM withtheshapeofsingle plateandstripisrelativelyeasy,anditsreversibilityincrystallographiciseasilytocarryout,fortheεM with multilayerstructure,thereversetrans formationtakes placein isolatedlayers, fortheεMthat grows well,thereversetransforma tion isrelatively difficult becauseofthe ductile harmonization between itsinternalorganiza tion structures.
关键词:
stress induced εM
,
null
,
null
徐佩
,
卢旭鑫
,
汪传斌
,
杨善中
,
孙晓红
,
丁运生
高分子材料科学与工程
为改善多壁碳纳米管(MWNT)在低密度聚乙烯(LDPE)中的分散性及复合材料的界面特性,采用溴化-1-十六烷基-3-甲基咪唑基离子液体([C16min]Br)对MWNT进行表面改性,并用Raman光谱对改性效果进行了表征.将经过修饰的碳纳米管(MIL)与LDPE熔融共混得到MIL/LDPE复合材料,采用场发射扫描电子显微镜(FESEM)和阻抗分析仪(LCR)对复合材料的结构与介电性能进行了分析.结果表明,相比与MWNT/LDPE(渗流阈值为5.2％,介电常数为82,介电损耗为0.93),MIL/LDPE(渗流阈值为9.1％,介电常数为169,介电损耗为0.51)介电常数增大,介电损耗降低.并且在低温时,MIL/LDPE介电常数随温度的变化甚小,显示出良好的温度-介电常数特性.
关键词:
咪唑基离子液体
,
碳纳米管
,
低密度聚乙烯
,
介电性能
Journal of Materials Research
Based on the best bulk metallic glass (BMG) forming alloy in the Mg-Cu-Y ternary system, we introduced Ag (or Ni) to partially substitute for Cu to improve the glass-forming ability (GFA). The objective of this paper is twofold. First, we illustrate in detail a recently developed search strategy, which was proposed but only briefly outlined in our previous publication [H. Ma, L.L. Shi, J. Xu, Y. Li, and E. Ma: Discovering inch-diameter metallic glasses in three-dimensional composition space. Appl. Phys. Lett. 87, 181915 (2005)]. The protocol to navigate in three-dimensional composition space to land large BMGs is spelled out step-by-step using the pseudo-ternary Mg-(Cu,Ag)-Y as the model system. Second, our ability to locate the best BMG former in the composition tetrahedron allows us to systematically examine, and conclude on, the effects of a given alloying element. The large improvement in glass-forming ability in the Mg-(Cu,Ag)-Y system relative to the based ternary will be contrasted with the reduced glass-forming ability in the Mg-(Cu,Ni)-Y pseudo ternary system. It is demonstrated that the improvement of glass-forming ability requires judicious choice of substitutional alloying elements and concentrations, rather than simple additions of multiple elements assuming the "confusion principle."
关键词:
bulk metallic-glass;shaped copper mold;amorphous-alloys;thermal-stability;ternary-system;casting method;p system;diameter;zr;mm
孙保基
,
张葆
,
宋策
,
龙思源
液晶与显示
doi:10.3788/YJYXS20163109.0921
针对TLD算法的特征点无法有效表述目标问题，提出了一种基于角点增强改进的TLD目标跟踪算法。改进算法在跟踪模块加入了对目标表述能力更强，具有光照不敏感性和旋转不变性的 Shi-Tomas 角点作为跟踪特征点。跟踪器运行时，在角点经光流法跟踪和双向误差检测后，利用剩余的稳定角点定位目标窗口。对照结果表明，改进算法在面对目标抖动和形变时可以稳定跟踪；有效抑制因跟踪平滑点造成的漂移现象；提高了跟踪的稳定性。针对 TLD算法跟踪过程中因在线模板积累造成的计算量持续增大、实时性持续降低的问题，提出了一种依据相似度中值的模板判断删除机制。该删除机制在模板积累到设定阈值时运行，根据模板与当前目标的相似度，删除不再具备代表性的模板；调整模板空间并更新模板数目。实验表明，该删除机制在应对模板更新快、持续时间长的跟踪情景时有效降低算法计算量，实时性可提高约20％。
关键词:
目标跟踪
,
TLD
,
角点特征
,
在线模板
王玉东
,
付鹏
,
李晓光
,
刘民英
,
赵清香
高分子材料科学与工程
用差示扫描量热(DSC)研究了尼龙612的等温结晶动力学.实验结果表明,在所研究的等温结晶温度范围内(184℃、186℃、188℃、190℃、192℃),尼龙612达到最大结晶速率时的时间、半结晶期和动力学结晶速率常数分别为:O.12min、0.19 min、0.22 min、0.29 min、0.59 min;0.15 min、0.22 min、0.24 min、0.33 min、0.64 min和22.03 min<'-1>、23.28min<'-1>、8.85 min<'-1>、5.15 min<'-1>、1.93 min<'-1>.等温结晶过程符合Avrmi方程,二次结晶现象不明显.在等温结晶过程中得到的Avrmi指数n在1.81～2.32之间,由理论分析可知,尼龙612等温结晶是一维生长和二维盘状生长.由Arrhenius方程求得尼龙612的等温结晶活化能ΔE=-209.5 kJ/mol.
关键词:
尼龙612
,
等温结晶动力学
,
结晶活化能
靳瑞敏
,
陈兰莉
,
罗鹏辉
,
郭新峰
,
卢景霄
材料导报
用玻璃作衬底在不同温度下用PECVD法直接沉积非晶硅(a-Si∶H)薄膜,在400℃和500℃分别光退火5min、10min、20min、30min、40min、60min、120min,用拉曼光谱分析前后样品,发现随着晶化时间的延长晶化效果越好,500℃退火的薄膜比400℃的晶化效果好.
关键词:
PECVD法
,
非晶硅薄膜
,
光退火晶化
,
拉曼光谱
殷红旗
,
刘永长
,
宁保群
,
徐荣雷
,
张尧卿
,
韩雅静
材料科学与工程学报
doi:10.3969/j.issn.1673-2812.2007.01.030
本文研究了T91钢冷却过程中,不同冷却速度(10 k/min(200 k/min)对相变速度和产物的影响.研究表明不同的冷却速度生成的组织差别较大,在较低速冷却下(10 k/min和30 k/min)的组织为较多的先共析铁素体和板条马氏体,中速冷却(30 k/min和50 k/min)基本都为板条马氏体,在较高速冷却过程中(100 k/min和200 k/min)组织中除了板条马氏体还出现了片状马氏体,另外冷却速度还影响了相变开始点和相变速度.
关键词:
T91
,
冷却速度
,
相变