Performance of Polyaniline-coated Short Carbon Fibers in Electromagnetic Shielding Coating

Dongxiu YU , Jiang CHENG

材料科学技术(英文)

Combined nitric acid oxidation method and polyaniline (PANI)-coated method were applied to modify the surface properties of short carbon fibers (SCF). The electrical and mechanical properties of acrylic coatings with 50 wt pct PANI-coated carbon fiber were investigated by using scanning electron microscope (SEM), UVVis spectrophotometer, four-probe method and the coaxial cable method. The results of the pH measurement and XPS (X-ray photoelectron spectroscopy) patterns showed that the oxygen functional groups, such as -OH and -COOH, were attached on the carbon fiber surfaces after oxidation treatment. The XPS analysis of PANI-coated oxidized SCF (PAOSCF) revealed that PANI may bond on the surface of oxidized SCF with chemical bonds. SEM images and surface roughness analyses showed that PANI-coated layer changed the surface morphology. Compared with SCF/acrylic coating, the surface resistivity of PAOSCF/acrylic coating decreased from17.1 to 5.3 Ω/sq and the shielding efficiency (SE) value increased from 1.54 to 23.3 dB.

关键词: carbon fibers , 聚苯胺 , 表面处理 , 分散稳定性 , 屏蔽效

Morphologies and Superhydrophobicity of Hybrid Film Surfaces Based on Silica and Fluoropolymer

Ailan QU , Xiufang WEN , Pihui PI , Jiang CHENG , Zhuoru YANG

材料科学技术(英文)

Fluoropolymer and different kinds of silica particles were used for controlling surface chemistry and morphology, respectively. A superhydrophobic surface originated from strawberry-like or quincunx-shaped composite silica particles was obtained. The dual size particles are obtained by utilizing the graft of different modified silica particles with epoxy functional group and amine functional group. This makes the surface of film form a composite interface to have irregular binary structure which plays an essential role in trapping air between the substrate surface and the liquid droplets to be necessary for high contact angle and low contact angle hysteresis. The maximum contact angle for water on the hybrid film is about 174±2° and the contact angle hysteresis is less than 2°. The surface morphologies, roughness and the wettability on the surface of films containing different structural silica particles were compared. It was shown that the hierarchical irregularly structure with a low roughness factor and high air-trapped ratio is indispensable for superhydrophobic surface. Although this structural surfaces based on composite silica particles play a vital role in governing the surface wettability, it is necessary to combine with a low surface energy to make the surface superhydrophobic.

关键词: Superhydrophobicity , 双微观结构 , 纳米复合粒子 , 含氟硅