S.J. Yao
,
L.X. Du
,
X.H. Liu
,
G.D. Wang
金属学报(英文版)
Three warm-rolled ferrite/pearlite microstructures
were prepared by rolling at 500℃, and the austenitizing
characteristics were discussed in conjunction with deformation
during the heating stage. The results indicated that the final
austenite grain size was sensitive to the deformation direction of
the initial warm-rolled microstructure. The transient microstructure
at a given temperature was the most important influencing factor on
the austenitizing characteristic combined with deformation.
Moreover, the hot-rolled microstructure also had to be prepared in
an optimal state because of its direct effect on the warm-rolled
microstructure.
关键词:
Warm-rolled ferrite/pearlite
,
null
,
null
G.M. Cao
,
C.G. Li
,
Z.Y. Liu
,
D. Wu
,
G.D. Wang
,
X.H. Liu
金属学报(英文版)
Coupled turbulent flow, temperature fields of the twin-roll casting strip process were simulated by three-dimensional finite element method. Based on the heat balance calculation and using inverse methods between the simulations and real experiments, the relational models among casting speed, location, and coefficient of heat transfer between molten metal and rolls in different regions are given. In the simulation, the calculated surface temperatures are in good agreement with the measured values. An on-line model of kiss point is derived by simulations and the geometry of molten
pool, corresponding control strategy is also proposed.
关键词:
Twin-roll strip casting
,
null
J.X. Li
,
X.H. Liu
,
G.D. Wang
金属学报(英文版)
Two kinds of cold rolling experiments, single cold rolling and double cold rolling, werecarried out on one titanium stabilized interstitial free (IF) steel that has been warmrolled at ferrite temperature. The main aim was to investigate the evolution of rollingand annealing textures from the well known behavior observed under single cold rollingcondition to the less understood double cold rolling by using orientation distributionfunction (ODF). In the twice cold rolled samples, the annealing texture comprises onlyfirst round of rolling. Accordingly both the once cold rolled sample and the twice coldrolled sample with heavy reduction in the first round of rolling have much complextexture components. They are related to the formation of initial {111} subgrain andthe priority growth of stable {111} nucleus.