Cracking morphology in the fusion zone of HQ130 high strength steel was researched by "the y-silt test" and "three point bend test", ultrasonic test and microscope. HQ130+QJ63 high strength steel was welded by Ar+CO2 gas shielded arc welding under the condition of no-preheat. Experimental results indicated that welding crack produced in the partially melted zone of the weld root of HQ130 steel side and propagated parallel to the fusion zone. The cracking developed alternatively between the weld and the partially melted zone, and is not strictly to rupture at W/F boundary surface. Controlling weld heat input (E) about 16 kJ/cm could make the cracking rate to be lowest and satisfy the performance requirement of welded joint zone.
关键词:
High strength steel
,
null
,
null
Yajiang LI
,
Zengda ZOU
,
Bing ZHOU
材料科学技术（英）
Microstructure and alloy element distribution in the welded joint between austenitic stainless steel (1Cr18Ni9Ti) and pearlitic heat-resistant steel (1Cr5Mo) were researched by means of light microscopy, scanning electron microscopy (SEM) and electron probe microanalysis (EPMA). Microstructure, divisions of the fusion zone and elemental diffusion distributions in the welded joints were investigated. Furthermore, solidification microstructure and S-ferrite distribution in the weld metal of these steels are also discussed.
关键词: